Kraiburg TPE THERMOLAST? K TC4PCN Thermoplastic Elastomer, Adhesion to PA, optimised compression set

Kraiburg TPE THERMOLAST? K TC4PCN Thermoplastic Elastomer, Adhesion to PA, optimised compression set 物性表: Kraiburg TPE THERMOLAST? K TC4PCN Thermoplastic Elastomer, Adhesion to PA, optimised compression set物性表及特性介紹,Kraiburg TPE THERMOLAST? K TC4PCN Thermoplastic Elastomer, Adhesion to PA, optimised compression set注塑參數(shù)詳情,如需Kraiburg TPE THERMOLAST? K TC4PCN Thermoplastic Elastomer, Adhesion to PA, optimised compression set下載, 可到相關(guān)下載區(qū)下載

密度 [g/cm3]: 1.1

Physical Properties	Metric	English	Comments

Density	1.10 g/cc	0.0397 lb/in3	DIN EN ISO 1183-1:2004

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	40	40	DIN 53505 / ISO 868
Tensile Strength at Break	2.70 MPa	392 psi	Deviating from ISO 37 standard test piece S2 is tested with a traverse speed of 200 mm/min; DIN 53504 / ISO 37
Elongation at Break	300 %	300 %	Deviating from ISO 37 standard test piece S2 is tested with a traverse speed of 200 mm/min; DIN 53504 / ISO 37
Peel Strength	8.00 kN/m	45.6 pli	to PA 6.6; Renault test D41 1916
	11.0 kN/m	62.8 pli	to PA 6; Renault test D41 1916
Graves Tear Strength	8.00 kN/m	45.6 pli	DIN ISO 34-1 Method B (b)
Compression Set	14 % @Temperature 23.0 °C, Time 259000 sec	14 % @Temperature 73.4 °F, Time 72.0 hour	ISO 815
	27 % @Temperature 70.0 °C, Time 79200 sec	27 % @Temperature 158 °F, Time 22.0 hour	ISO 815
	51 % @Temperature 100 °C, Time 79200 sec	51 % @Temperature 212 °F, Time 22.0 hour	ISO 815

Thermal Properties	Metric	English	Comments
Flammability, UL94	HB	HB

Processing Properties	Metric	English	Comments
Processing Temperature	240 - 270 °C	464 - 518 °F	adhesion to PA 6
	255 - 280 °C	491 - 536 °F	adhesion to PA 6.6 and polyamide
Mold Temperature	40.0 - 60.0 °C	104 - 140 °F
Drying Temperature	60.0 - 80.0 °C @Time 7200 - 14400 sec	140 - 176 °F @Time 2.00 - 4.00 hour	Pre drying

Descriptive Properties
Color	Natural

關(guān)鍵詞:
TPE
供應(yīng)
Adhesion to PA
optimised compression set
Kraiburg TPE THERMOLAST? K TC4PCN Thermoplastic Elastomer

轉(zhuǎn)載請注明: 轉(zhuǎn)自中國塑膠原料之家 http://www.spnmy.cn/wuxingbiao/

本文鏈接: http://www.spnmy.cn/yuanliaoku/show-48709.html

免責(zé)聲明: 本文 Kraiburg TPE THERMOLAST? K TC4PCN Thermoplastic Elastomer, Adhesion to PA, optimised compression set 僅代表作者個人觀點，中國塑膠原料之家無關(guān)。中國塑膠原料之家網(wǎng)所轉(zhuǎn)載的內(nèi)容，其版權(quán)均由原作者和資料提供方所擁有！如因作品版權(quán)問題需要處理，請與我們聯(lián)絡(luò)