- 彎曲強度 [MPa]: 4.83
- 脆化溫度 [℃]: -65.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.900 g/cc | 0.900 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 40 | 40 | Instantaneous; ASTM D2240 |
| Tensile Strength, Ultimate | 4.83 MPa | 700 psi | Method A (Dumbbell & Section), 20 in/min, Break; ASTM D412 |
| Elongation at Break | 700 % | 700 % | Method A (Dumbbell & Section), 20 in/min; ASTM D412 |
| 300% Modulus | 0.00231 GPa | 0.335 ksi | Method A (Dumbbell & Section), 20 in/min; ASTM D412 |
| Rebound | 57 % | 57 % | Bayshore; ASTM D2632 |
| Tear Strength | 20.2 kN/m | 115 pli | Die C (graves), 20 in/min; ASTM D624 |
| Compression Set | 20 % | 20 % | Method B, 73°F (23°C), 22 hrs; ASTM D395 |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | -65.0 °C | -85.0 °F | ASTM D746 |