- 拉伸強(qiáng)度 [MPa]: 6.89
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.900 g/cc | 0.900 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0269 cm/cm | 0.0269 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 41 | 41 | Instant; ASTM D2240 |
| Tensile Strength, Yield | 6.89 MPa | 1000 psi | Method A (Dumbbell & Section), 20 in/min, Break; ASTM D412 |
| 2.55 MPa @Strain 300 % | 370 psi @Strain 300 % | Method A (Dumbbell & Section), 20 in/min; ASTM D412 | |
| Elongation at Break | 800 % | 800 % | Method A (Dumbbell & Section), 20 in/min; ASTM D412 |
| Tear Strength | 29.8 kN/m | 170 pli | Die C (graves), 20 in/min; ASTM D624 |
| Compression Set | 22 % | 22 % | Method B, 73°F(23°C), 22 hrs; ASTM D395 |
| Optical Properties | Metric | English | Comments |
| Transmission, Visible | 90.0 % | 90.0 % | transparent; thickness not quantified |