- 彎曲強度 [MPa]: 5.93
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.890 g/cc | 0.890 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 65 | 65 | Instantaneous; ASTM D2240 |
| Tensile Strength, Ultimate | 5.93 MPa | 860 psi | Method A (Dumbbell & Section), 20 in/min, Break; ASTM D412 |
| Elongation at Break | 515 % | 515 % | Method A (Dumbbell & Section), 20 in/min; ASTM D412 |
| 100% Modulus | 0.00272 GPa | 0.395 ksi | Method A (Dumbbell & Section), 20 in/min; ASTM D412 |
| 300% Modulus | 0.00414 GPa | 0.600 ksi | Method A (Dumbbell & Section), 20 in/min; ASTM D412 |
| Tear Strength | 28.0 kN/m | 160 pli | Die C (graves), 20 in/min; ASTM D624 |
| Compression Set | 26 % | 26 % | Method B, 73°F (23°C), 22 hrs; ASTM D395 |
| 36 % | 36 % | Method B, 104°F (40°C), 22 hrs; ASTM D395 | |
| 47 % | 47 % | Method B, 158°F (70°C), 22 hrs; ASTM D395 | |