- 拉伸強度 [MPa]: 4.31
- 脆化溫度 [℃]: -62.5
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.22 g/cc | 1.22 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0126 cm/cm | 0.0126 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 28 | 28 | 10 Sec; ASTM D2240 |
| Tensile Strength, Yield | 4.31 MPa | 625 psi | Method A (Dumbbell & Section), 20 in/min, Break; ASTM D412 |
| 4.14 MPa @Strain 300 % | 600 psi @Strain 300 % | Method A (Dumbbell & Section), 20 in/min; ASTM D412 | |
| Elongation at Break | 375 % | 375 % | Method A (Dumbbell & Section), 20 in/min; ASTM D412 |
| Tear Strength | 34.2 kN/m | 195 pli | Die C (graves), 20 in/min; ASTM D624 |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | -62.5 °C | -80.5 °F | ASTM D746 |