- 缺口沖擊強(qiáng)度: 5.7
- 彎曲模量 [MPa]: 6.25
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 3.80 g/cc | 3.80 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.010 - 0.012 cm/cm | 0.010 - 0.012 in/in | Internal |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 27.0 MPa | 3920 psi | ISO 527 |
| Elongation at Break | 0.50 % | 0.50 % | ISO 527 |
| Tensile Modulus | 7.583 GPa | 1100 ksi | ISO 527 |
| Flexural Modulus | 6.25 GPa | 906 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 5.70 kJ/m2 | 2.71 ft-lb/in2 | ISO 180-A |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 230 - 250 °C | 446 - 482 °F | |
| Mold Temperature | 65.0 - 80.0 °C | 149 - 176 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 4 - 6 hour | 4 - 6 hour | |
| Moisture Content | <= 0.20 % | <= 0.20 % | |