- 密度 [g/cm3]: 1.08
- 吸水率 [%]: 0.58
- 拉伸強(qiáng)度 [MPa]: 47.0
- 彎曲模量 [MPa]: 1.90
- 熱變形溫度 [℃]: 151.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.08 g/cc | 0.0390 lb/in3 | DAM; ISO 1183 | ||
| Water Absorption | 0.58 % @Temperature 23.0 °C | 0.58 % @Temperature 73.4 °F | Immersion 24h; DAM; ISO 62, Similar to | ||
| Linear Mold Shrinkage, Flow | 0.012 cm/cm @Thickness 2.00 mm | 0.012 in/in @Thickness 0.0787 in | Parallel; DAM; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.012 cm/cm @Thickness 2.00 mm | 0.012 in/in @Thickness 0.0787 in | Normal; DAM; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Stress | 0.0300 MPa @Strain 0.000 %, Temperature 60.0 °C | 4.35 psi @Strain 0.000 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | ||
| 0.0600 MPa @Strain 0.000 %, Temperature 40.0 °C | 8.70 psi @Strain 0.000 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 0.0700 MPa @Strain 0.000 %, Temperature 60.0 °C | 10.2 psi @Strain 0.000 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 0.0700 MPa @Strain 0.000 %, Temperature 90.0 °C | 10.2 psi @Strain 0.000 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 0.0900 MPa @Strain 0.000 %, Temperature 150 °C | 13.1 psi @Strain 0.000 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 0.0900 MPa @Strain 0.000 %, Temperature 120 °C | 13.1 psi @Strain 0.000 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 0.0900 MPa @Strain 0.000 %, Temperature 120 °C | 13.1 psi @Strain 0.000 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 0.100 MPa @Strain 0.000 %, Temperature 150 °C | 14.5 psi @Strain 0.000 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 0.100 MPa @Strain 0.000 %, Temperature 90.0 °C | 14.5 psi @Strain 0.000 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 0.200 MPa @Strain 0.000 %, Temperature 40.0 °C | 29.0 psi @Strain 0.000 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 0.220 MPa @Strain 0.000 %, Temperature 23.0 °C | 31.9 psi @Strain 0.000 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 0.330 MPa @Strain 0.000 %, Temperature 0.000 °C | 47.9 psi @Strain 0.000 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 0.340 MPa @Strain 0.000 %, Temperature -40.0 °C | 49.3 psi @Strain 0.000 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 0.360 MPa @Strain 0.000 %, Temperature -20.0 °C | 52.2 psi @Strain 0.000 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 0.410 MPa @Strain 0.000 %, Temperature -20.0 °C | 59.5 psi @Strain 0.000 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 0.410 MPa @Strain 0.000 %, Temperature -40.0 °C | 59.5 psi @Strain 0.000 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
| 0.450 MPa @Strain 0.000 %, Temperature 0.000 °C | 65.3 psi @Strain 0.000 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 0.460 MPa @Strain 0.000 %, Temperature 23.0 °C | 66.7 psi @Strain 0.000 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 0.500 MPa @Strain 0.0300 %, Temperature -40.0 °C | 72.5 psi @Strain 0.0300 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
| 0.520 MPa @Strain 0.0900 %, Temperature 60.0 °C | 75.4 psi @Strain 0.0900 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 0.620 MPa @Strain 0.0200 %, Temperature -40.0 °C | 89.9 psi @Strain 0.0200 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 0.790 MPa @Strain 0.110 %, Temperature 40.0 °C | 115 psi @Strain 0.110 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 0.980 MPa @Strain 0.180 %, Temperature 60.0 °C | 142 psi @Strain 0.180 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 1.02 MPa @Strain 0.0600 %, Temperature -40.0 °C | 148 psi @Strain 0.0600 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
| 1.15 MPa @Strain 0.0500 %, Temperature -40.0 °C | 167 psi @Strain 0.0500 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 1.16 MPa @Strain 0.0400 %, Temperature -20.0 °C | 168 psi @Strain 0.0400 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 1.21 MPa @Strain 0.0100 %, Temperature -40.0 °C | 175 psi @Strain 0.0100 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
| 1.32 MPa @Strain 0.0800 %, Temperature 23.0 °C | 191 psi @Strain 0.0800 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 1.37 MPa @Strain 0.100 %, Temperature 40.0 °C | 199 psi @Strain 0.100 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 1.46 MPa @Strain 0.200 %, Temperature 40.0 °C | 212 psi @Strain 0.200 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 1.51 MPa @Strain 0.0500 %, Temperature -20.0 °C | 219 psi @Strain 0.0500 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 1.55 MPa @Strain 0.0900 %, Temperature -40.0 °C | 225 psi @Strain 0.0900 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
| 1.81 MPa @Strain 0.0600 %, Temperature 0.000 °C | 263 psi @Strain 0.0600 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 1.96 MPa @Strain 0.0800 %, Temperature -40.0 °C | 284 psi @Strain 0.0800 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 1.98 MPa @Strain 0.0700 %, Temperature 23.0 °C | 287 psi @Strain 0.0700 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 2.04 MPa @Strain 0.0700 %, Temperature -20.0 °C | 296 psi @Strain 0.0700 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 2.05 MPa @Strain 0.110 %, Temperature -40.0 °C | 297 psi @Strain 0.110 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
| 2.06 MPa @Strain 0.0700 %, Temperature 0.000 °C | 299 psi @Strain 0.0700 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 2.38 MPa @Strain 0.160 %, Temperature 23.0 °C | 345 psi @Strain 0.160 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 2.52 MPa @Strain 0.180 %, Temperature 40.0 °C | 365 psi @Strain 0.180 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 2.56 MPa @Strain 0.130 %, Temperature -40.0 °C | 371 psi @Strain 0.130 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
| 2.68 MPa @Strain 0.100 %, Temperature -20.0 °C | 389 psi @Strain 0.100 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 2.78 MPa @Strain 0.130 %, Temperature -40.0 °C | 403 psi @Strain 0.130 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 2.84 MPa @Strain 0.110 %, Temperature -20.0 °C | 412 psi @Strain 0.110 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 2.87 MPa @Strain 0.720 %, Temperature 90.0 °C | 416 psi @Strain 0.720 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 2.91 MPa @Strain 1.12 %, Temperature 150 °C | 422 psi @Strain 1.12 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 3.09 MPa @Strain 0.150 %, Temperature -40.0 °C | 448 psi @Strain 0.150 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
| 3.15 MPa @Strain 0.120 %, Temperature 0.000 °C | 457 psi @Strain 0.120 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 3.42 MPa @Strain 0.240 %, Temperature 23.0 °C | 496 psi @Strain 0.240 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 3.52 MPa @Strain 0.150 %, Temperature 23.0 °C | 511 psi @Strain 0.150 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 3.62 MPa @Strain 0.170 %, Temperature -40.0 °C | 525 psi @Strain 0.170 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
| 3.62 MPa @Strain 0.160 %, Temperature -40.0 °C | 525 psi @Strain 0.160 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 3.66 MPa @Strain 0.140 %, Temperature 0.000 °C | 531 psi @Strain 0.140 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 3.73 MPa @Strain 0.140 %, Temperature -20.0 °C | 541 psi @Strain 0.140 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 3.86 MPa @Strain 0.140 %, Temperature -20.0 °C | 560 psi @Strain 0.140 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 4.10 MPa @Strain 0.190 %, Temperature -40.0 °C | 595 psi @Strain 0.190 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
| 4.38 MPa @Strain 0.180 %, Temperature -40.0 °C | 635 psi @Strain 0.180 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 4.48 MPa @Strain 0.170 %, Temperature -20.0 °C | 650 psi @Strain 0.170 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 4.49 MPa @Strain 0.180 %, Temperature 0.000 °C | 651 psi @Strain 0.180 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 4.63 MPa @Strain 0.220 %, Temperature -40.0 °C | 672 psi @Strain 0.220 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
| 4.83 MPa @Strain 0.850 %, Temperature 60.0 °C | 701 psi @Strain 0.850 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 4.88 MPa @Strain 0.180 %, Temperature -20.0 °C | 708 psi @Strain 0.180 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 5.02 MPa @Strain 0.220 %, Temperature 23.0 °C | 728 psi @Strain 0.220 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 5.11 MPa @Strain 0.230 %, Temperature -40.0 °C | 741 psi @Strain 0.230 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
| 5.15 MPa @Strain 0.200 %, Temperature -40.0 °C | 747 psi @Strain 0.200 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 5.20 MPa @Strain 0.200 %, Temperature -20.0 °C | 754 psi @Strain 0.200 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 5.21 MPa @Strain 0.200 %, Temperature 0.000 °C | 756 psi @Strain 0.200 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 5.82 MPa @Strain 0.230 %, Temperature -20.0 °C | 844 psi @Strain 0.230 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 5.85 MPa @Strain 0.240 %, Temperature 0.000 °C | 848 psi @Strain 0.240 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 5.87 MPa @Strain 0.230 %, Temperature -40.0 °C | 851 psi @Strain 0.230 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 6.00 MPa @Strain 0.230 %, Temperature -20.0 °C | 870 psi @Strain 0.230 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 6.79 MPa @Strain 0.420 %, Temperature 40.0 °C | 985 psi @Strain 0.420 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 6.82 MPa @Strain 0.250 %, Temperature 0.000 °C | 989 psi @Strain 0.250 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 7.32 MPa @Strain 2.81 %, Temperature 120 °C | 1060 psi @Strain 2.81 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 7.64 MPa @Strain 4.83 %, Temperature 150 °C | 1110 psi @Strain 4.83 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 7.66 MPa @Strain 0.340 %, Temperature -40.0 °C | 1110 psi @Strain 0.340 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
| 8.73 MPa @Strain 2.34 %, Temperature 90.0 °C | 1270 psi @Strain 2.34 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 11.24 MPa @Strain 1.36 %, Temperature 40.0 °C | 1630 psi @Strain 1.36 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 11.29 MPa @Strain 4.42 %, Temperature 120 °C | 1637 psi @Strain 4.42 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 12.67 MPa @Strain 19.61 %, Temperature 150 °C | 1838 psi @Strain 19.61 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 13.66 MPa @Strain 15.4 %, Temperature 150 °C | 1981 psi @Strain 15.4 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 13.9 MPa @Strain 35.77 %, Temperature 150 °C | 2020 psi @Strain 35.77 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 14.22 MPa @Strain 74.79 %, Temperature 150 °C | 2062 psi @Strain 74.79 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 14.32 MPa @Strain 53.66 %, Temperature 150 °C | 2077 psi @Strain 53.66 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 14.5 MPa @Strain 97.79 %, Temperature 150 °C | 2100 psi @Strain 97.79 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 14.71 MPa @Strain 120.22 %, Temperature 150 °C | 2134 psi @Strain 120.22 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 14.82 MPa @Strain 0.560 %, Temperature -20.0 °C | 2149 psi @Strain 0.560 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 14.91 MPa @Strain 140.41 %, Temperature 150 °C | 2163 psi @Strain 140.41 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 15.03 MPa @Strain 151.24 %, Temperature 150 °C | 2180 psi @Strain 151.24 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 15.09 MPa @Strain 155.64 %, Temperature 150 °C | 2189 psi @Strain 155.64 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 15.41 MPa @Strain 31.09 %, Temperature 150 °C | 2235 psi @Strain 31.09 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 15.56 MPa @Strain 159.24 %, Temperature 150 °C | 2257 psi @Strain 159.24 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 16.03 MPa @Strain 48.0 %, Temperature 150 °C | 2325 psi @Strain 48.0 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 16.07 MPa @Strain 4.08 %, Temperature 60.0 °C | 2331 psi @Strain 4.08 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 16.16 MPa @Strain 162.13 %, Temperature 150 °C | 2344 psi @Strain 162.13 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 16.21 MPa @Strain 66.5 %, Temperature 150 °C | 2351 psi @Strain 66.5 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 16.28 MPa @Strain 86.91 %, Temperature 150 °C | 2361 psi @Strain 86.91 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 16.48 MPa @Strain 108.08 %, Temperature 150 °C | 2390 psi @Strain 108.08 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 16.56 MPa @Strain 16.72 %, Temperature 120 °C | 2402 psi @Strain 16.72 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 16.75 MPa @Strain 127.64 %, Temperature 150 °C | 2429 psi @Strain 127.64 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 17.01 MPa @Strain 143.1 %, Temperature 150 °C | 2467 psi @Strain 143.1 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 17.35 MPa @Strain 153.75 %, Temperature 150 °C | 2516 psi @Strain 153.75 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 17.51 MPa @Strain 167.77 %, Temperature 150 °C | 2540 psi @Strain 167.77 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 17.63 MPa @Strain 160.48 %, Temperature 150 °C | 2557 psi @Strain 160.48 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 18.03 MPa @Strain 165.47 %, Temperature 150 °C | 2615 psi @Strain 165.47 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 18.36 MPa @Strain 32.34 %, Temperature 120 °C | 2663 psi @Strain 32.34 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 18.67 MPa @Strain 179.08 %, Temperature 150 °C | 2708 psi @Strain 179.08 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 18.75 MPa @Strain 18.38 %, Temperature 120 °C | 2719 psi @Strain 18.38 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 18.92 MPa @Strain 49.29 %, Temperature 120 °C | 2744 psi @Strain 49.29 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 19.0 MPa @Strain 68.28 %, Temperature 120 °C | 2760 psi @Strain 68.28 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 19.03 MPa @Strain 89.58 %, Temperature 120 °C | 2760 psi @Strain 89.58 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 19.15 MPa @Strain 0.760 %, Temperature -40.0 °C | 2777 psi @Strain 0.760 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 19.28 MPa @Strain 171.78 %, Temperature 150 °C | 2796 psi @Strain 171.78 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 19.38 MPa @Strain 111.08 %, Temperature 120 °C | 2811 psi @Strain 111.08 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 19.53 MPa @Strain 193.77 %, Temperature 150 °C | 2833 psi @Strain 193.77 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 19.65 MPa @Strain 130.59 %, Temperature 120 °C | 2850 psi @Strain 130.59 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 19.81 MPa @Strain 13.57 %, Temperature 90.0 °C | 2873 psi @Strain 13.57 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 19.92 MPa @Strain 146.76 %, Temperature 120 °C | 2889 psi @Strain 146.76 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 20.16 MPa @Strain 158.86 %, Temperature 120 °C | 2924 psi @Strain 158.86 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 20.26 MPa @Strain 34.15 %, Temperature 120 °C | 2938 psi @Strain 34.15 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 20.31 MPa @Strain 181.42 %, Temperature 150 °C | 2946 psi @Strain 181.42 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 20.44 MPa @Strain 209.25 %, Temperature 150 °C | 2965 psi @Strain 209.25 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 20.45 MPa @Strain 165.43 %, Temperature 120 °C | 2966 psi @Strain 165.43 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 20.74 MPa @Strain 51.1 %, Temperature 120 °C | 3008 psi @Strain 51.1 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 20.78 MPa @Strain 168.96 %, Temperature 120 °C | 3014 psi @Strain 168.96 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 20.86 MPa @Strain 69.53 %, Temperature 120 °C | 3025 psi @Strain 69.53 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 20.93 MPa @Strain 89.3 %, Temperature 120 °C | 3036 psi @Strain 89.3 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 21.08 MPa @Strain 195.61 %, Temperature 150 °C | 3057 psi @Strain 195.61 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 21.18 MPa @Strain 109.3 %, Temperature 120 °C | 3072 psi @Strain 109.3 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 21.35 MPa @Strain 222.8 %, Temperature 150 °C | 3097 psi @Strain 222.8 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 21.49 MPa @Strain 7.55 %, Temperature 60.0 °C | 3117 psi @Strain 7.55 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 21.58 MPa @Strain 127.93 %, Temperature 120 °C | 3130 psi @Strain 127.93 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 21.89 MPa @Strain 143.39 %, Temperature 120 °C | 3175 psi @Strain 143.39 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 21.96 MPa @Strain 211.7 %, Temperature 150 °C | 3185 psi @Strain 211.7 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 22.22 MPa @Strain 173.45 %, Temperature 120 °C | 3223 psi @Strain 173.45 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 22.22 MPa @Strain 155.42 %, Temperature 120 °C | 3223 psi @Strain 155.42 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 22.37 MPa @Strain 233.96 %, Temperature 150 °C | 3245 psi @Strain 233.96 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 22.46 MPa @Strain 28.79 %, Temperature 90.0 °C | 3258 psi @Strain 28.79 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 22.57 MPa @Strain 163.93 %, Temperature 120 °C | 3274 psi @Strain 163.93 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 22.62 MPa @Strain 15.36 %, Temperature 90.0 °C | 3281 psi @Strain 15.36 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 22.95 MPa @Strain 0.930 %, Temperature -20.0 °C | 3329 psi @Strain 0.930 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 22.96 MPa @Strain 226.76 %, Temperature 150 °C | 3330 psi @Strain 226.76 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 23.03 MPa @Strain 170.05 %, Temperature 120 °C | 3340 psi @Strain 170.05 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 23.07 MPa @Strain 45.7 %, Temperature 90.0 °C | 3346 psi @Strain 45.7 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 23.18 MPa @Strain 64.6 %, Temperature 90.0 °C | 3362 psi @Strain 64.6 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 23.26 MPa @Strain 85.33 %, Temperature 90.0 °C | 3374 psi @Strain 85.33 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 23.35 MPa @Strain 4.27 %, Temperature 40.0 °C | 3387 psi @Strain 4.27 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 23.42 MPa @Strain 244.24 %, Temperature 150 °C | 3397 psi @Strain 244.24 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 23.59 MPa @Strain 106.23 %, Temperature 90.0 °C | 3421 psi @Strain 106.23 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 23.62 MPa @Strain 181.4 %, Temperature 120 °C | 3426 psi @Strain 181.4 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 23.93 MPa @Strain 238.87 %, Temperature 150 °C | 3471 psi @Strain 238.87 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 23.96 MPa @Strain 125.44 %, Temperature 90.0 °C | 3475 psi @Strain 125.44 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 24.13 MPa @Strain 175.88 %, Temperature 120 °C | 3500 psi @Strain 175.88 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 24.31 MPa @Strain 141.59 %, Temperature 90.0 °C | 3526 psi @Strain 141.59 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 24.42 MPa @Strain 194.77 %, Temperature 120 °C | 3542 psi @Strain 194.77 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 24.46 MPa @Strain 254.22 %, Temperature 150 °C | 3548 psi @Strain 254.22 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 24.53 MPa @Strain 11.23 %, Temperature 60.0 °C | 3558 psi @Strain 11.23 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 24.65 MPa @Strain 153.4 %, Temperature 90.0 °C | 3575 psi @Strain 153.4 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 24.99 MPa @Strain 249.42 %, Temperature 150 °C | 3624 psi @Strain 249.42 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 25.03 MPa @Strain 160.71 %, Temperature 90.0 °C | 3630 psi @Strain 160.71 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 25.11 MPa @Strain 30.67 %, Temperature 90.0 °C | 3642 psi @Strain 30.67 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 25.11 MPa @Strain 1.17 %, Temperature 23.0 °C | 3642 psi @Strain 1.17 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 25.32 MPa @Strain 211.15 %, Temperature 120 °C | 3672 psi @Strain 211.15 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 25.43 MPa @Strain 184.18 %, Temperature 120 °C | 3688 psi @Strain 184.18 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 25.46 MPa @Strain 263.78 %, Temperature 150 °C | 3693 psi @Strain 263.78 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 25.48 MPa @Strain 165.5 %, Temperature 90.0 °C | 3696 psi @Strain 165.5 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 25.82 MPa @Strain 47.28 %, Temperature 90.0 °C | 3745 psi @Strain 47.28 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 26.09 MPa @Strain 64.98 %, Temperature 90.0 °C | 3784 psi @Strain 64.98 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 26.1 MPa @Strain 259.54 %, Temperature 150 °C | 3790 psi @Strain 259.54 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 26.25 MPa @Strain 289.42 %, Temperature 150 °C | 3807 psi @Strain 289.42 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 26.31 MPa @Strain 15.11 %, Temperature 60.0 °C | 3816 psi @Strain 15.11 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 26.33 MPa @Strain 83.5 %, Temperature 90.0 °C | 3819 psi @Strain 83.5 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 26.38 MPa @Strain 196.7 %, Temperature 120 °C | 3826 psi @Strain 196.7 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 26.44 MPa @Strain 227.21 %, Temperature 120 °C | 3835 psi @Strain 227.21 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 26.49 MPa @Strain 273.35 %, Temperature 150 °C | 3842 psi @Strain 273.35 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 26.66 MPa @Strain 102.17 %, Temperature 90.0 °C | 3867 psi @Strain 102.17 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 26.86 MPa @Strain 1.18 %, Temperature -40.0 °C | 3896 psi @Strain 1.18 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
| 26.87 MPa @Strain 170.68 %, Temperature 90.0 °C | 3897 psi @Strain 170.68 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 27.07 MPa @Strain 120 %, Temperature 90.0 °C | 3926 psi @Strain 120 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 27.22 MPa @Strain 269.68 %, Temperature 150 °C | 3948 psi @Strain 269.68 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 27.28 MPa @Strain 212.26 %, Temperature 120 °C | 3957 psi @Strain 212.26 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 27.31 MPa @Strain 2.04 %, Temperature 23.0 °C | 3961 psi @Strain 2.04 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 27.39 MPa @Strain 19.15 %, Temperature 60.0 °C | 3973 psi @Strain 19.15 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 27.49 MPa @Strain 282.43 %, Temperature 150 °C | 3987 psi @Strain 282.43 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 27.56 MPa @Strain 136.01 %, Temperature 90.0 °C | 3997 psi @Strain 136.01 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 28.02 MPa @Strain 9.91 %, Temperature 60.0 °C | 4064 psi @Strain 9.91 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 28.05 MPa @Strain 23.33 %, Temperature 60.0 °C | 4068 psi @Strain 23.33 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 28.07 MPa @Strain 149.23 %, Temperature 90.0 °C | 4071 psi @Strain 149.23 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 28.35 MPa @Strain 179 %, Temperature 90.0 °C | 4112 psi @Strain 179 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 28.36 MPa @Strain 279.55 %, Temperature 150 °C | 4113 psi @Strain 279.55 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 28.44 MPa @Strain 228.07 %, Temperature 120 °C | 4125 psi @Strain 228.07 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 28.45 MPa @Strain 27.7 %, Temperature 60.0 °C | 4126 psi @Strain 27.7 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 28.56 MPa @Strain 159.66 %, Temperature 90.0 °C | 4142 psi @Strain 159.66 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 28.57 MPa @Strain 250.88 %, Temperature 120 °C | 4144 psi @Strain 250.88 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 28.68 MPa @Strain 32.19 %, Temperature 60.0 °C | 4160 psi @Strain 32.19 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 28.8 MPa @Strain 36.82 %, Temperature 60.0 °C | 4180 psi @Strain 36.82 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 28.86 MPa @Strain 67.07 %, Temperature 60.0 °C | 4186 psi @Strain 67.07 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 28.87 MPa @Strain 41.54 %, Temperature 60.0 °C | 4187 psi @Strain 41.54 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 28.87 MPa @Strain 61.74 %, Temperature 60.0 °C | 4187 psi @Strain 61.74 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 28.87 MPa @Strain 72.48 %, Temperature 60.0 °C | 4187 psi @Strain 72.48 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 28.88 MPa @Strain 56.51 %, Temperature 60.0 °C | 4189 psi @Strain 56.51 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 28.89 MPa @Strain 46.41 %, Temperature 60.0 °C | 4190 psi @Strain 46.41 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 28.89 MPa @Strain 51.42 %, Temperature 60.0 °C | 4190 psi @Strain 51.42 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 28.9 MPa @Strain 77.94 %, Temperature 60.0 °C | 4190 psi @Strain 77.94 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 28.93 MPa @Strain 83.46 %, Temperature 60.0 °C | 4196 psi @Strain 83.46 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 28.98 MPa @Strain 89.0 %, Temperature 60.0 °C | 4203 psi @Strain 89.0 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 29.01 MPa @Strain 7.58 %, Temperature 40.0 °C | 4208 psi @Strain 7.58 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 29.09 MPa @Strain 94.56 %, Temperature 60.0 °C | 4219 psi @Strain 94.56 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 29.19 MPa @Strain 100.03 %, Temperature 60.0 °C | 4234 psi @Strain 100.03 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 29.22 MPa @Strain 167.94 %, Temperature 90.0 °C | 4238 psi @Strain 167.94 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 29.22 MPa @Strain 297.02 %, Temperature 150 °C | 4238 psi @Strain 297.02 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 29.25 MPa @Strain 192.14 %, Temperature 90.0 °C | 4242 psi @Strain 192.14 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 29.54 MPa @Strain 288.97 %, Temperature 150 °C | 4284 psi @Strain 288.97 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 29.57 MPa @Strain 241.83 %, Temperature 120 °C | 4289 psi @Strain 241.83 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 29.85 MPa @Strain 260.89 %, Temperature 120 °C | 4329 psi @Strain 260.89 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 30.08 MPa @Strain 175.17 %, Temperature 90.0 °C | 4363 psi @Strain 175.17 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 30.25 MPa @Strain 208.44 %, Temperature 90.0 °C | 4387 psi @Strain 208.44 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 30.74 MPa @Strain 253.08 %, Temperature 120 °C | 4458 psi @Strain 253.08 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 31.06 MPa @Strain 270.86 %, Temperature 120 °C | 4505 psi @Strain 270.86 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 31.43 MPa @Strain 183.29 %, Temperature 90.0 °C | 4559 psi @Strain 183.29 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 31.53 MPa @Strain 224.82 %, Temperature 90.0 °C | 4573 psi @Strain 224.82 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 32.08 MPa @Strain 263.03 %, Temperature 120 °C | 4653 psi @Strain 263.03 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 32.25 MPa @Strain 298.44 %, Temperature 120 °C | 4677 psi @Strain 298.44 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 32.29 MPa @Strain 280.79 %, Temperature 120 °C | 4683 psi @Strain 280.79 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 32.38 MPa @Strain 11.02 %, Temperature 40.0 °C | 4696 psi @Strain 11.02 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 32.71 MPa @Strain 194.32 %, Temperature 90.0 °C | 4744 psi @Strain 194.32 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 32.73 MPa @Strain 238.67 %, Temperature 90.0 °C | 4747 psi @Strain 238.67 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 33.45 MPa @Strain 272.65 %, Temperature 120 °C | 4852 psi @Strain 272.65 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 33.58 MPa @Strain 290.42 %, Temperature 120 °C | 4870 psi @Strain 290.42 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 33.67 MPa @Strain 208.77 %, Temperature 90.0 °C | 4883 psi @Strain 208.77 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 34.01 MPa @Strain 249.49 %, Temperature 90.0 °C | 4933 psi @Strain 249.49 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 34.31 MPa @Strain 32.7 %, Temperature 60.0 °C | 4976 psi @Strain 32.7 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 34.4 MPa @Strain 14.65 %, Temperature 40.0 °C | 4990 psi @Strain 14.65 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 34.79 MPa @Strain 299.81 %, Temperature 120 °C | 5046 psi @Strain 299.81 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 34.8 MPa @Strain 282.18 %, Temperature 120 °C | 5050 psi @Strain 282.18 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 34.89 MPa @Strain 224.91 %, Temperature 90.0 °C | 5060 psi @Strain 224.91 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 35.04 MPa @Strain 88.17 %, Temperature 40.0 °C | 5082 psi @Strain 88.17 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 35.05 MPa @Strain 94.08 %, Temperature 40.0 °C | 5084 psi @Strain 94.08 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 35.11 MPa @Strain 58.35 %, Temperature 60.0 °C | 5092 psi @Strain 58.35 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 35.12 MPa @Strain 82.32 %, Temperature 40.0 °C | 5094 psi @Strain 82.32 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 35.16 MPa @Strain 100.03 %, Temperature 40.0 °C | 5100 psi @Strain 100.03 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 35.18 MPa @Strain 76.56 %, Temperature 40.0 °C | 5102 psi @Strain 76.56 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 35.25 MPa @Strain 86.62 %, Temperature 60.0 °C | 5113 psi @Strain 86.62 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 35.27 MPa @Strain 2.72 %, Temperature 40.0 °C | 5115 psi @Strain 2.72 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 35.28 MPa @Strain 70.92 %, Temperature 40.0 °C | 5117 psi @Strain 70.92 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 35.43 MPa @Strain 65.38 %, Temperature 40.0 °C | 5139 psi @Strain 65.38 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 35.48 MPa @Strain 259.18 %, Temperature 90.0 °C | 5146 psi @Strain 259.18 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 35.51 MPa @Strain 18.44 %, Temperature 40.0 °C | 5150 psi @Strain 18.44 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 35.59 MPa @Strain 60.0 %, Temperature 40.0 °C | 5162 psi @Strain 60.0 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 35.59 MPa @Strain 117.56 %, Temperature 60.0 °C | 5162 psi @Strain 117.56 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 35.72 MPa @Strain 54.73 %, Temperature 40.0 °C | 5181 psi @Strain 54.73 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 35.87 MPa @Strain 1.60 %, Temperature 0.000 °C | 5203 psi @Strain 1.60 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 35.89 MPa @Strain 49.63 %, Temperature 40.0 °C | 5205 psi @Strain 49.63 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 36.06 MPa @Strain 44.72 %, Temperature 40.0 °C | 5230 psi @Strain 44.72 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 36.08 MPa @Strain 22.41 %, Temperature 40.0 °C | 5233 psi @Strain 22.41 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 36.2 MPa @Strain 39.95 %, Temperature 40.0 °C | 5250 psi @Strain 39.95 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 36.22 MPa @Strain 291.52 %, Temperature 120 °C | 5253 psi @Strain 291.52 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 36.31 MPa @Strain 35.32 %, Temperature 40.0 °C | 5266 psi @Strain 35.32 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 36.31 MPa @Strain 240.37 %, Temperature 90.0 °C | 5266 psi @Strain 240.37 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 36.32 MPa @Strain 26.58 %, Temperature 40.0 °C | 5268 psi @Strain 26.58 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 36.37 MPa @Strain 30.88 %, Temperature 40.0 °C | 5275 psi @Strain 30.88 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 36.53 MPa @Strain 147.51 %, Temperature 60.0 °C | 5298 psi @Strain 147.51 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 36.93 MPa @Strain 268.65 %, Temperature 90.0 °C | 5356 psi @Strain 268.65 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 37.08 MPa @Strain 171.45 %, Temperature 60.0 °C | 5378 psi @Strain 171.45 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 37.64 MPa @Strain 188.45 %, Temperature 60.0 °C | 5459 psi @Strain 188.45 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 37.65 MPa @Strain 253.42 %, Temperature 90.0 °C | 5461 psi @Strain 253.42 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 38.18 MPa @Strain 197.17 %, Temperature 60.0 °C | 5538 psi @Strain 197.17 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 38.38 MPa @Strain 278.23 %, Temperature 90.0 °C | 5567 psi @Strain 278.23 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 38.52 MPa @Strain 58.29 %, Temperature 23.0 °C | 5587 psi @Strain 58.29 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 38.87 MPa @Strain 64.25 %, Temperature 23.0 °C | 5638 psi @Strain 64.25 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 38.98 MPa @Strain 263.82 %, Temperature 90.0 °C | 5654 psi @Strain 263.82 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 39.09 MPa @Strain 70.2 %, Temperature 23.0 °C | 5670 psi @Strain 70.2 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 39.17 MPa @Strain 76.19 %, Temperature 23.0 °C | 5681 psi @Strain 76.19 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 39.2 MPa @Strain 82.16 %, Temperature 23.0 °C | 5690 psi @Strain 82.16 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 39.2 MPa @Strain 88.11 %, Temperature 23.0 °C | 5690 psi @Strain 88.11 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 39.32 MPa @Strain 94.1 %, Temperature 23.0 °C | 5703 psi @Strain 94.1 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 39.48 MPa @Strain 100.04 %, Temperature 23.0 °C | 5726 psi @Strain 100.04 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 39.81 MPa @Strain 297.04 %, Temperature 90.0 °C | 5774 psi @Strain 297.04 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 39.85 MPa @Strain 4.94 %, Temperature 23.0 °C | 5780 psi @Strain 4.94 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 39.94 MPa @Strain 287.93 %, Temperature 90.0 °C | 5793 psi @Strain 287.93 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 40.12 MPa @Strain 201.44 %, Temperature 60.0 °C | 5819 psi @Strain 201.44 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 40.24 MPa @Strain 308.97 %, Temperature 60.0 °C | 5836 psi @Strain 308.97 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 40.31 MPa @Strain 69.11 %, Temperature 40.0 °C | 5846 psi @Strain 69.11 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 40.47 MPa @Strain 308.95 %, Temperature 60.0 °C | 5870 psi @Strain 308.95 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 40.51 MPa @Strain 272.69 %, Temperature 90.0 °C | 5875 psi @Strain 272.69 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 40.74 MPa @Strain 308.93 %, Temperature 60.0 °C | 5909 psi @Strain 308.93 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 40.87 MPa @Strain 75.22 %, Temperature 40.0 °C | 5928 psi @Strain 75.22 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 41.01 MPa @Strain 6.16 %, Temperature 40.0 °C | 5948 psi @Strain 6.16 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 41.05 MPa @Strain 308.91 %, Temperature 60.0 °C | 5954 psi @Strain 308.91 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 41.17 MPa @Strain 81.35 %, Temperature 40.0 °C | 5971 psi @Strain 81.35 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 41.24 MPa @Strain 87.53 %, Temperature 40.0 °C | 5981 psi @Strain 87.53 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 41.29 MPa @Strain 93.78 %, Temperature 40.0 °C | 5989 psi @Strain 93.78 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 41.34 MPa @Strain 100.05 %, Temperature 40.0 °C | 5996 psi @Strain 100.05 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 41.42 MPa @Strain 308.89 %, Temperature 60.0 °C | 6007 psi @Strain 308.89 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 41.89 MPa @Strain 308.86 %, Temperature 60.0 °C | 6076 psi @Strain 308.86 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 42.08 MPa @Strain 281.37 %, Temperature 90.0 °C | 6103 psi @Strain 281.37 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 42.09 MPa @Strain 51.8 %, Temperature 23.0 °C | 6105 psi @Strain 51.8 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 42.28 MPa @Strain 9.84 %, Temperature 40.0 °C | 6132 psi @Strain 9.84 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 42.45 MPa @Strain 62.72 %, Temperature 40.0 °C | 6157 psi @Strain 62.72 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 42.53 MPa @Strain 308.82 %, Temperature 60.0 °C | 6168 psi @Strain 308.82 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 43.0 MPa @Strain 1.82 %, Temperature -20.0 °C | 6240 psi @Strain 1.82 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 43.06 MPa @Strain 8.32 %, Temperature 23.0 °C | 6245 psi @Strain 8.32 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 43.24 MPa @Strain 299.33 %, Temperature 90.0 °C | 6271 psi @Strain 299.33 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 43.56 MPa @Strain 13.49 %, Temperature 40.0 °C | 6318 psi @Strain 13.49 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 43.58 MPa @Strain 308.78 %, Temperature 60.0 °C | 6321 psi @Strain 308.78 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 43.66 MPa @Strain 56.94 %, Temperature 40.0 °C | 6332 psi @Strain 56.94 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 43.74 MPa @Strain 290.29 %, Temperature 90.0 °C | 6344 psi @Strain 290.29 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 43.96 MPa @Strain 25.78 %, Temperature 23.0 °C | 6376 psi @Strain 25.78 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 44.18 MPa @Strain 2.02 %, Temperature -40.0 °C | 6408 psi @Strain 2.02 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
| 44.19 MPa @Strain 210.69 %, Temperature 60.0 °C | 6409 psi @Strain 210.69 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 44.23 MPa @Strain 51.62 %, Temperature 40.0 °C | 6415 psi @Strain 51.62 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 44.36 MPa @Strain 31.7 %, Temperature 23.0 °C | 6434 psi @Strain 31.7 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 44.43 MPa @Strain 37.71 %, Temperature 23.0 °C | 6444 psi @Strain 37.71 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 44.43 MPa @Strain 43.69 %, Temperature 23.0 °C | 6444 psi @Strain 43.69 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 44.44 MPa @Strain 17.18 %, Temperature 40.0 °C | 6445 psi @Strain 17.18 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 44.48 MPa @Strain 49.65 %, Temperature 23.0 °C | 6451 psi @Strain 49.65 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 44.52 MPa @Strain 239.49 %, Temperature 60.0 °C | 6457 psi @Strain 239.49 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 44.57 MPa @Strain 55.64 %, Temperature 23.0 °C | 6464 psi @Strain 55.64 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 44.62 MPa @Strain 46.61 %, Temperature 40.0 °C | 6472 psi @Strain 46.61 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 44.66 MPa @Strain 45.8 %, Temperature 23.0 °C | 6477 psi @Strain 45.8 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 44.78 MPa @Strain 61.63 %, Temperature 23.0 °C | 6495 psi @Strain 61.63 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 44.89 MPa @Strain 41.86 %, Temperature 40.0 °C | 6511 psi @Strain 41.86 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 44.91 MPa @Strain 67.58 %, Temperature 23.0 °C | 6514 psi @Strain 67.58 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 44.96 MPa @Strain 20.95 %, Temperature 40.0 °C | 6521 psi @Strain 20.95 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 44.97 MPa @Strain 79.02 %, Temperature 23.0 °C | 6522 psi @Strain 79.02 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 45.01 MPa @Strain 73.54 %, Temperature 23.0 °C | 6528 psi @Strain 73.54 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 45.08 MPa @Strain 79.39 %, Temperature 23.0 °C | 6538 psi @Strain 79.39 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 45.08 MPa @Strain 74.75 %, Temperature 23.0 °C | 6538 psi @Strain 74.75 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 45.1 MPa @Strain 83.88 %, Temperature 23.0 °C | 6540 psi @Strain 83.88 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 45.12 MPa @Strain 37.36 %, Temperature 40.0 °C | 6544 psi @Strain 37.36 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 45.23 MPa @Strain 24.82 %, Temperature 40.0 °C | 6560 psi @Strain 24.82 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 45.24 MPa @Strain 89.11 %, Temperature 23.0 °C | 6562 psi @Strain 89.11 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 45.26 MPa @Strain 33.02 %, Temperature 40.0 °C | 6564 psi @Strain 33.02 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 45.29 MPa @Strain 11.68 %, Temperature 23.0 °C | 6569 psi @Strain 11.68 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 45.33 MPa @Strain 28.87 %, Temperature 40.0 °C | 6575 psi @Strain 28.87 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 45.4 MPa @Strain 94.51 %, Temperature 23.0 °C | 6580 psi @Strain 94.51 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 45.45 MPa @Strain 100.06 %, Temperature 23.0 °C | 6592 psi @Strain 100.06 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 45.99 MPa @Strain 1.98 %, Temperature -40.0 °C | 6670 psi @Strain 1.98 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 46.04 MPa @Strain 40.35 %, Temperature 23.0 °C | 6678 psi @Strain 40.35 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 46.78 MPa @Strain 15.1 %, Temperature 23.0 °C | 6785 psi @Strain 15.1 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 46.93 MPa @Strain 35.33 %, Temperature 23.0 °C | 6807 psi @Strain 35.33 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 46.93 MPa @Strain 308.81 %, Temperature 60.0 °C | 6807 psi @Strain 308.81 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 47.47 MPa @Strain 269.11 %, Temperature 60.0 °C | 6885 psi @Strain 269.11 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 47.47 MPa @Strain 46.7 %, Temperature 0.000 °C | 6885 psi @Strain 46.7 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 47.53 MPa @Strain 30.69 %, Temperature 23.0 °C | 6894 psi @Strain 30.69 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 47.6 MPa @Strain 18.65 %, Temperature 23.0 °C | 6900 psi @Strain 18.65 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 47.86 MPa @Strain 26.41 %, Temperature 23.0 °C | 6942 psi @Strain 26.41 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 47.92 MPa @Strain 22.41 %, Temperature 23.0 °C | 6950 psi @Strain 22.41 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 47.94 MPa @Strain 52.62 %, Temperature 0.000 °C | 6953 psi @Strain 52.62 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 48.28 MPa @Strain 64.49 %, Temperature 0.000 °C | 7002 psi @Strain 64.49 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 48.31 MPa @Strain 58.53 %, Temperature 0.000 °C | 7007 psi @Strain 58.53 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 48.4 MPa @Strain 70.4 %, Temperature 0.000 °C | 7020 psi @Strain 70.4 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 48.63 MPa @Strain 82.27 %, Temperature 0.000 °C | 7053 psi @Strain 82.27 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 48.72 MPa @Strain 76.32 %, Temperature 0.000 °C | 7066 psi @Strain 76.32 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 48.88 MPa @Strain 100.05 %, Temperature 0.000 °C | 7089 psi @Strain 100.05 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 48.93 MPa @Strain 88.16 %, Temperature 0.000 °C | 7097 psi @Strain 88.16 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 48.93 MPa @Strain 94.1 %, Temperature 0.000 °C | 7097 psi @Strain 94.1 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 48.99 MPa @Strain 2.27 %, Temperature 0.000 °C | 7105 psi @Strain 2.27 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 50.5 MPa @Strain 289.24 %, Temperature 60.0 °C | 7320 psi @Strain 289.24 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 50.62 MPa @Strain 40.3 %, Temperature -20.0 °C | 7342 psi @Strain 40.3 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 50.98 MPa @Strain 74.43 %, Temperature -20.0 °C | 7394 psi @Strain 74.43 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 51.17 MPa @Strain 30.94 %, Temperature 0.000 °C | 7422 psi @Strain 30.94 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 51.41 MPa @Strain 50.0 %, Temperature -20.0 °C | 7456 psi @Strain 50.0 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 51.47 MPa @Strain 45.14 %, Temperature -20.0 °C | 7465 psi @Strain 45.14 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 51.57 MPa @Strain 54.8 %, Temperature -20.0 °C | 7480 psi @Strain 54.8 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 51.71 MPa @Strain 59.63 %, Temperature -20.0 °C | 7500 psi @Strain 59.63 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 51.72 MPa @Strain 303.18 %, Temperature 60.0 °C | 7501 psi @Strain 303.18 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 51.76 MPa @Strain 46.01 %, Temperature 0.000 °C | 7507 psi @Strain 46.01 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 51.83 MPa @Strain 92.14 %, Temperature 0.000 °C | 7517 psi @Strain 92.14 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 51.83 MPa @Strain 64.46 %, Temperature -20.0 °C | 7517 psi @Strain 64.46 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 51.85 MPa @Strain 86.28 %, Temperature 0.000 °C | 7520 psi @Strain 86.28 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 51.85 MPa @Strain 40.96 %, Temperature 0.000 °C | 7520 psi @Strain 40.96 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 51.86 MPa @Strain 35.92 %, Temperature 0.000 °C | 7522 psi @Strain 35.92 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 51.92 MPa @Strain 51.03 %, Temperature 0.000 °C | 7530 psi @Strain 51.03 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 51.99 MPa @Strain 56.07 %, Temperature 0.000 °C | 7541 psi @Strain 56.07 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 51.99 MPa @Strain 69.26 %, Temperature -20.0 °C | 7541 psi @Strain 69.26 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 52.02 MPa @Strain 61.09 %, Temperature 0.000 °C | 7545 psi @Strain 61.09 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 52.18 MPa @Strain 66.1 %, Temperature 0.000 °C | 7568 psi @Strain 66.1 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 52.24 MPa @Strain 76.16 %, Temperature 0.000 °C | 7577 psi @Strain 76.16 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 52.27 MPa @Strain 71.14 %, Temperature 0.000 °C | 7581 psi @Strain 71.14 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 52.38 MPa @Strain 81.18 %, Temperature 0.000 °C | 7597 psi @Strain 81.18 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 54.13 MPa @Strain 29.47 %, Temperature -20.0 °C | 7851 psi @Strain 29.47 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 54.14 MPa @Strain 25.55 %, Temperature -20.0 °C | 7852 psi @Strain 25.55 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 54.47 MPa @Strain 18.92 %, Temperature 23.0 °C | 7900 psi @Strain 18.92 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 54.5 MPa @Strain 33.22 %, Temperature -20.0 °C | 7900 psi @Strain 33.22 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 54.58 MPa @Strain 36.96 %, Temperature -20.0 °C | 7916 psi @Strain 36.96 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 54.65 MPa @Strain 52.29 %, Temperature -20.0 °C | 7926 psi @Strain 52.29 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 54.67 MPa @Strain 48.19 %, Temperature -20.0 °C | 7929 psi @Strain 48.19 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 54.69 MPa @Strain 44.43 %, Temperature -20.0 °C | 7932 psi @Strain 44.43 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 54.72 MPa @Strain 40.67 %, Temperature -20.0 °C | 7936 psi @Strain 40.67 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 56.19 MPa @Strain 2.76 %, Temperature -20.0 °C | 8150 psi @Strain 2.76 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 56.77 MPa @Strain 13.26 %, Temperature 23.0 °C | 8234 psi @Strain 13.26 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 57.77 MPa @Strain 39.63 %, Temperature 0.000 °C | 8379 psi @Strain 39.63 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 58.71 MPa @Strain 2.81 %, Temperature -40.0 °C | 8515 psi @Strain 2.81 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
| 58.92 MPa @Strain 7.92 %, Temperature 23.0 °C | 8546 psi @Strain 7.92 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 59.36 MPa @Strain 3.41 %, Temperature 23.0 °C | 8609 psi @Strain 3.41 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 60.81 MPa @Strain 24.98 %, Temperature 0.000 °C | 8820 psi @Strain 24.98 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 62.99 MPa @Strain 33.81 %, Temperature 0.000 °C | 9136 psi @Strain 33.81 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 64.12 MPa @Strain 5.20 %, Temperature 0.000 °C | 9300 psi @Strain 5.20 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 64.55 MPa @Strain 28.89 %, Temperature 0.000 °C | 9362 psi @Strain 28.89 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 65.29 MPa @Strain 8.78 %, Temperature 0.000 °C | 9470 psi @Strain 8.78 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 65.3 MPa @Strain 3.17 %, Temperature -40.0 °C | 9470 psi @Strain 3.17 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 65.33 MPa @Strain 24.42 %, Temperature 0.000 °C | 9475 psi @Strain 24.42 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 65.64 MPa @Strain 20.29 %, Temperature 0.000 °C | 9520 psi @Strain 20.29 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 65.74 MPa @Strain 12.52 %, Temperature 0.000 °C | 9535 psi @Strain 12.52 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 65.95 MPa @Strain 16.35 %, Temperature 0.000 °C | 9565 psi @Strain 16.35 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 66.32 MPa @Strain 3.20 %, Temperature -20.0 °C | 9619 psi @Strain 3.20 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 66.8 MPa @Strain 3.56 %, Temperature 0.000 °C | 9690 psi @Strain 3.56 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 68.21 MPa @Strain 19.51 %, Temperature 0.000 °C | 9893 psi @Strain 19.51 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 69.37 MPa @Strain 33.66 %, Temperature -20.0 °C | 10060 psi @Strain 33.66 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 70.2 MPa @Strain 14.8 %, Temperature 0.000 °C | 10200 psi @Strain 14.8 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 70.39 MPa @Strain 3.61 %, Temperature -40.0 °C | 10210 psi @Strain 3.61 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
| 72.53 MPa @Strain 10.37 %, Temperature 0.000 °C | 10520 psi @Strain 10.37 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 73.17 MPa @Strain 4.99 %, Temperature -20.0 °C | 10610 psi @Strain 4.99 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 73.84 MPa @Strain 28.93 %, Temperature -20.0 °C | 10710 psi @Strain 28.93 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 74.44 MPa @Strain 20.08 %, Temperature -20.0 °C | 10800 psi @Strain 20.08 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 75.47 MPa @Strain 24.79 %, Temperature -20.0 °C | 10950 psi @Strain 24.79 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 75.93 MPa @Strain 6.37 %, Temperature 0.000 °C | 11010 psi @Strain 6.37 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 76.42 MPa @Strain 21.0 %, Temperature -20.0 °C | 11080 psi @Strain 21.0 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 77.02 MPa @Strain 17.44 %, Temperature -20.0 °C | 11170 psi @Strain 17.44 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 77.21 MPa @Strain 7.78 %, Temperature -20.0 °C | 11200 psi @Strain 7.78 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 77.55 MPa @Strain 14.06 %, Temperature -20.0 °C | 11250 psi @Strain 14.06 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 77.79 MPa @Strain 10.82 %, Temperature -20.0 °C | 11280 psi @Strain 10.82 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 77.95 MPa @Strain 16.33 %, Temperature -20.0 °C | 11310 psi @Strain 16.33 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 78.05 MPa @Strain 4.41 %, Temperature -40.0 °C | 11320 psi @Strain 4.41 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 79.79 MPa @Strain 4.47 %, Temperature -40.0 °C | 11570 psi @Strain 4.47 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
| 80.26 MPa @Strain 12.91 %, Temperature -20.0 °C | 11640 psi @Strain 12.91 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 80.89 MPa @Strain 4.84 %, Temperature -20.0 °C | 11730 psi @Strain 4.84 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 82.38 MPa @Strain 9.81 %, Temperature -20.0 °C | 11950 psi @Strain 9.81 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 84.04 MPa @Strain 7.06 %, Temperature -20.0 °C | 12190 psi @Strain 7.06 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 85.15 MPa @Strain 29.24 %, Temperature -40.0 °C | 12350 psi @Strain 29.24 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 85.91 MPa @Strain 5.80 %, Temperature -40.0 °C | 12460 psi @Strain 5.80 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 86.55 MPa @Strain 5.41 %, Temperature -40.0 °C | 12550 psi @Strain 5.41 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
| 86.65 MPa @Strain 26.47 %, Temperature -40.0 °C | 12570 psi @Strain 26.47 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 88.13 MPa @Strain 11.01 %, Temperature -40.0 °C | 12780 psi @Strain 11.01 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
| 88.63 MPa @Strain 24.06 %, Temperature -40.0 °C | 12850 psi @Strain 24.06 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 89.05 MPa @Strain 10.68 %, Temperature -40.0 °C | 12920 psi @Strain 10.68 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
| 89.79 MPa @Strain 7.45 %, Temperature -40.0 °C | 13020 psi @Strain 7.45 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 89.95 MPa @Strain 21.7 %, Temperature -40.0 °C | 13050 psi @Strain 21.7 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 90.45 MPa @Strain 6.44 %, Temperature -40.0 °C | 13120 psi @Strain 6.44 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
| 90.98 MPa @Strain 19.44 %, Temperature -40.0 °C | 13200 psi @Strain 19.44 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 91.13 MPa @Strain 9.89 %, Temperature -40.0 °C | 13220 psi @Strain 9.89 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
| 91.28 MPa @Strain 9.24 %, Temperature -40.0 °C | 13240 psi @Strain 9.24 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 91.59 MPa @Strain 17.29 %, Temperature -40.0 °C | 13280 psi @Strain 17.29 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 91.62 MPa @Strain 15.17 %, Temperature -40.0 °C | 13290 psi @Strain 15.17 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 91.63 MPa @Strain 13.1 %, Temperature -40.0 °C | 13290 psi @Strain 13.1 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 91.7 MPa @Strain 11.15 %, Temperature -40.0 °C | 13300 psi @Strain 11.15 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 91.95 MPa @Strain 7.63 %, Temperature -40.0 °C | 13340 psi @Strain 7.63 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
| 91.99 MPa @Strain 8.79 %, Temperature -40.0 °C | 13340 psi @Strain 8.79 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
| Tensile Strength, Yield | 47.0 MPa @Temperature 23.0 °C | 6820 psi @Temperature 73.4 °F | DAM; ISO 527 | ||
| Elongation at Break | 258 % @Temperature 23.0 °C | 258 % @Temperature 73.4 °F | DAM; ISO 527 | ||
| Tensile Modulus | 0.213 GPa @Temperature 150 °C | 30.9 ksi @Temperature 302 °F | 50%RH; ISO 11403-1/-2 | ||
| 0.227 GPa @Temperature 150 °C | 32.9 ksi @Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 0.272 GPa @Temperature 120 °C | 39.5 ksi @Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 0.309 GPa @Temperature 120 °C | 44.8 ksi @Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 0.357 GPa @Temperature 90.0 °C | 51.8 ksi @Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 0.375 GPa @Temperature 90.0 °C | 54.4 ksi @Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 0.500 GPa @Temperature 60.0 °C | 72.5 ksi @Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 0.602 GPa @Temperature 60.0 °C | 87.3 ksi @Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 0.717 GPa @Temperature 40.0 °C | 104 ksi @Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 1.254 GPa @Temperature 23.0 °C | 181.9 ksi @Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 1.349 GPa @Temperature 40.0 °C | 195.7 ksi @Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 2.055 GPa @Temperature 23.0 °C | 298.1 ksi @Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 2.313 GPa @Temperature 0.000 °C | 335.5 ksi @Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 2.315 GPa @Temperature 23.0 °C | 335.8 ksi @Temperature 73.4 °F | DAM; ISO 527 | |||
| 2.316 GPa @Temperature -40.0 °C | 335.9 ksi @Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
| 2.32 GPa @Temperature -20.0 °C | 336 ksi @Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 2.374 GPa @Temperature -20.0 °C | 344.3 ksi @Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 2.458 GPa @Temperature 0.000 °C | 356.5 ksi @Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 2.459 GPa @Temperature -40.0 °C | 356.6 ksi @Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
| Flexural Strength | 86.0 MPa @Temperature 23.0 °C | 12500 psi @Temperature 73.4 °F | DAM; ISO 178 | ||
| Flexural Modulus | 1.90 GPa @Temperature 23.0 °C | 276 ksi @Temperature 73.4 °F | DAM; ISO 178 | ||
| Charpy Impact Unnotched | NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | DAM; ISO 179/1eU | ||
| Charpy Impact, Notched | 0.560 J/cm2 @Temperature 23.0 °C | 2.66 ft-lb/in2 @Temperature 73.4 °F | DAM; ISO 179/1eA | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 151 °C | 304 °F | DAM; ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C | 129 °F | DAM; ISO 75-1/-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 225 °C | 437 °F | 10°C/min; DAM; ISO 11357-1/-3 | ||
| 240 °C | 464 °F | DAM; Optimum; Extrusion | |||
| 235 - 245 °C | 455 - 473 °F | DAM; Extrusion | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM; Extrusion | ||
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour | DAM; Extrusion | ||
| Moisture Content | <= 0.050 % | <= 0.050 % | DAM; Extrusion | ||
| Descriptive Properties | |||||
| Appearance | Natural Color | DAM | |||
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | DAM | |||
| Features | Chemical Resistance, Good | DAM | |||
| Dimensional Stability, Good | DAM | ||||
| Flexibility, Good | DAM | ||||
| Moisture Absorption, Low | DAM | ||||
| Renewable Resource Content | DAM | ||||
| Viscosity, High | DAM | ||||
| Forms | Pellets | DAM | |||
| Generic | PA610 | DAM | |||
| Material Status | Preliminary Data | DAM | |||
| Part Marking Code | >PA610< | ISO 11469; DAM | |||
| Polymer Family | Polyamide | DAM | |||
| Polymer Type | PA610 | DAM | |||
| Processing Method | Extrusion | DAM | |||
| Product Category | Extrusion Resins | DAM | |||
| Renewably Sourced Resins | DAM | ||||
| Unreinforced Resins | DAM | ||||
| Region Available - Global | Yes | DAM | |||
| Resin Identification | PA610 | ISO 1043; DAM | |||
| RoHS Compliance | Contact Manufacturer | DAM | |||
| Uses | Automotive Applications | DAM | |||
| Cable Jacketing | DAM | ||||
| Consumer Applications | DAM | ||||
| Filaments | DAM | ||||
| Hose | DAM | ||||
| Industrial Applications | DAM | ||||
| Tubing | DAM | ||||