- 密度 [g/cm3]: 1.32
- 缺口沖擊強度: 15.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.32 g/cc | 0.0477 lb/in3 | DAM; ISO 1183 | ||
| Filler Content | 30 % | 30 % | DAM | ||
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm @Thickness 2.00 mm | 0.0020 in/in @Thickness 0.0787 in | Parallel; DAM; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm @Thickness 2.00 mm | 0.0070 in/in @Thickness 0.0787 in | Normal; DAM; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 130 MPa @Temperature 23.0 °C | 18900 psi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 170 MPa @Temperature 23.0 °C | 24700 psi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Elongation at Break | 4.5 % @Temperature 23.0 °C | 4.5 % @Temperature 73.4 °F | DAM; ISO 527 | ||
| 6.5 % @Temperature 23.0 °C | 6.5 % @Temperature 73.4 °F | 50%RH; ISO 527 | |||
| Tensile Modulus | 6.80 GPa @Temperature 23.0 °C | 986 ksi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 8.50 GPa @Temperature 23.0 °C | 1230 ksi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Izod Impact, Notched (ISO) | 15.0 kJ/m2 @Temperature 23.0 °C | 7.14 ft-lb/in2 @Temperature 73.4 °F | DAM; ISO 180/1A | ||
| 16.0 kJ/m2 @Temperature 23.0 °C | 7.61 ft-lb/in2 @Temperature 73.4 °F | 50%RH; ISO 180/1A | |||
| Charpy Impact Unnotched | 9.50 J/cm2 @Temperature 23.0 °C | 45.2 ft-lb/in2 @Temperature 73.4 °F | DAM; ISO 179/1eU | ||
| 9.50 J/cm2 @Temperature 23.0 °C | 45.2 ft-lb/in2 @Temperature 73.4 °F | 50%RH; ISO 179/1eU | |||
| Charpy Impact, Notched | 1.50 J/cm2 @Temperature 23.0 °C | 7.14 ft-lb/in2 @Temperature 73.4 °F | DAM; ISO 179/1eA | ||
| 1.50 J/cm2 @Temperature 23.0 °C | 7.14 ft-lb/in2 @Temperature 73.4 °F | 50%RH; ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | DAM; ISO 75-1/-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 224 °C | 435 °F | 10°C/min; DAM; ISO 11357-1/-3 | ||
| 280 °C | 536 °F | DAM; Optimum | |||
| 260 - 300 °C | 500 - 572 °F | DAM | |||
| Mold Temperature | 80.0 °C | 176 °F | DAM; optimum | ||
| 70.0 - 90.0 °C | 158 - 194 °F | DAM | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM | ||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM | ||
| Moisture Content | <= 0.15 % | <= 0.15 % | DAM | ||
| Descriptive Properties | |||||
| Appearance | Black Color | DAM | |||
| Features | Renewable Resource Content | ||||
| Filler | Glass Reinforced | DAM | |||
| Forms | Pellets | DAM | |||
| Generic | Nylon 610 | DAM | |||
| Material Status | Preliminary Data | DAM | |||
| Part Marking Code | >PA610-GF30< | ISO 11469; DAM | |||
| Processing Method | Injection Molding | DAM | |||
| Product Category | Glass Reinforced Resins | DAM | |||
| Renewably Sourced Resins | DAM | ||||
| Region Available - Global | Yes | DAM | |||
| Resin Identification | PA610-GF30 | ISO 1043; DAM | |||
| RoHS Compliance | Contact Manufacturer | DAM | |||