- 密度 [g/cm3]: 1.08
- 缺口沖擊強度: 4.5
- 拉伸強度 [MPa]: 50.0
- 熱變形溫度 [℃]: 140.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.08 g/cc | 0.0390 lb/in3 | DAM; ISO 1183 | ||
| Linear Mold Shrinkage, Flow | 0.012 cm/cm @Thickness 2.00 mm | 0.012 in/in @Thickness 0.0787 in | Parallel; DAM; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.012 cm/cm @Thickness 2.00 mm | 0.012 in/in @Thickness 0.0787 in | Normal; DAM; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 50.0 MPa @Temperature 23.0 °C | 7250 psi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 65.0 MPa @Temperature 23.0 °C | 9430 psi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Elongation at Break | 40 % @Temperature 23.0 °C | 40 % @Temperature 73.4 °F | DAM; nominal; ISO 527 | ||
| 80 % @Temperature 23.0 °C | 80 % @Temperature 73.4 °F | 50mm/min; DAM; ISO 527 | |||
| 130 % @Temperature 23.0 °C | 130 % @Temperature 73.4 °F | 50%RH; nominal; ISO 527 | |||
| 200 % @Temperature 23.0 °C | 200 % @Temperature 73.4 °F | 50mm/min; 50%RH; ISO 527 | |||
| Elongation at Yield | 4.5 % @Temperature 23.0 °C | 4.5 % @Temperature 73.4 °F | DAM; ISO 527 | ||
| 25 % @Temperature 23.0 °C | 25 % @Temperature 73.4 °F | 50%RH; ISO 527 | |||
| Tensile Modulus | 1.30 GPa @Temperature 23.0 °C | 189 ksi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 2.20 GPa @Temperature 23.0 °C | 319 ksi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Izod Impact, Notched (ISO) | 4.50 kJ/m2 @Temperature 23.0 °C | 2.14 ft-lb/in2 @Temperature 73.4 °F | DAM; ISO 180/1A | ||
| 9.00 kJ/m2 @Temperature 23.0 °C | 4.28 ft-lb/in2 @Temperature 73.4 °F | 50%RH; ISO 180/1A | |||
| Charpy Impact Unnotched | NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | 50%RH; ISO 179/1eU | ||
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | DAM; ISO 179/1eU | |||
| Charpy Impact, Notched | 0.500 J/cm2 @Temperature 23.0 °C | 2.38 ft-lb/in2 @Temperature 73.4 °F | DAM; ISO 179/1eA | ||
| 1.10 J/cm2 @Temperature 23.0 °C | 5.23 ft-lb/in2 @Temperature 73.4 °F | 50%RH; ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 140 °C | 284 °F | DAM; ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | DAM; ISO 75-1/-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 223 °C | 433 °F | 10°C/min; DAM; ISO 11357-1/-3 | ||
| 260 °C | 500 °F | DAM; Optimum; Injection Molding | |||
| 250 - 270 °C | 482 - 518 °F | DAM; Injection Molding | |||
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | DAM; Injection Molding | ||
| 70.0 °C | 158 °F | DAM; optimum; Injection Molding | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM; Injection Molding | ||
| Dry Time | 4.00 - 6.00 hour | 4.00 - 6.00 hour | DAM; Injection Molding | ||
| Moisture Content | <= 0.10 % | <= 0.10 % | DAM; Injection Molding | ||
| Descriptive Properties | |||||
| Appearance | Black Color | DAM | |||
| Features | Renewable Resource Content | ||||
| Forms | Pellets | DAM | |||
| Generic | PA610 | DAM | |||
| Material Status | Preliminary Data | DAM | |||
| Part Marking Code | >PA610< | ISO 11469; DAM | |||
| Processing Method | Injection Molding | DAM | |||
| Product Category | Unreinforced Resins | DAM | |||
| Region Available - Global | Yes | DAM | |||
| Resin Identification | PA610 | ISO 1043; DAM | |||
| RoHS Compliance | Contact Manufacturer | DAM | |||