- 熔體流動速率 [g/10min]: 129.6
- 密度 [g/cm3]: 1.08
- 吸水率 [%]: 3.6
- 彎曲模量 [MPa]: 2.10
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.08 g/cc | 0.0390 lb/in3 | ISO 1183 | ||
| Water Absorption | 3.6 % | 3.6 % | ISO 62 | ||
| Moisture Absorption at Equilibrium | 1.4 % | 1.4 % | ISO 62 | ||
| Viscosity Measurement | 150 | 150 | [cm3/g]; ISO 307 | ||
| Linear Mold Shrinkage | 0.011 - 0.012 cm/cm | 0.011 - 0.012 in/in | Test Box 1.5 mm | ||
| Linear Mold Shrinkage, Flow | 0.016 cm/cm | 0.016 in/in | ISO 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.019 cm/cm | 0.019 in/in | ISO 2577 | ||
| Melt Flow | 129.6 g/10 min @Load 5.00 kg, Temperature 275 °C | 129.6 g/10 min @Load 11.0 lb, Temperature 527 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 50.0 MPa | 7250 psi | ISO 527-1/-2 | ||
| Elongation at Yield | 4.5 % | 4.5 % | ISO 527-1/-2 | ||
| Modulus of Elasticity | 2.40 GPa | 348 ksi | ISO 527-1/-2 | ||
| Flexural Strength | 85.0 MPa | 12300 psi | ISO 178 | ||
| Flexural Modulus | 2.10 GPa | 305 ksi | ISO 178 | ||
| Charpy Impact Unnotched | 30.0 J/cm2 @Temperature -30.0 °C | 143 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eU | ||
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 0.300 J/cm2 @Temperature -30.0 °C | 1.43 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eA | ||
| 0.500 J/cm2 @Temperature 23.0 °C | 2.38 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 220 °C | 428 °F | ISO 11357-1/-3 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 250 - 270 °C | 482 - 518 °F | Injection molding | ||
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | Injection molding/Extrusion | ||
| Descriptive Properties | |||||
| Commercial Status | Europe | ||||