- 熔體流動速率 [g/10min]: 5.0
- 密度 [g/cm3]: 1.15
- 吸水率 [%]: 0.1
- 缺口沖擊強度: 0.534
- 拉伸強度 [MPa]: 140.0
- 斷裂伸長率 [%]: 121
- 彎曲強度 [MPa]: 75.0
- 彎曲模量 [MPa]: 3.45
- 硬度: 117.0
- 熱變形溫度 [℃]: 207.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 - 1.63 g/cc | 0.0415 - 0.0589 lb/in3 | Average value: 1.37 g/cc Grade Count:72 |
| Filler Content | 10.0 - 50.0 % | 10.0 - 50.0 % | Average value: 29.1 % Grade Count:37 |
| Water Absorption | 0.100 - 4.00 % | 0.100 - 4.00 % | Average value: 1.02 % Grade Count:55 |
| Moisture Absorption at Equilibrium | 0.0900 - 1.30 % | 0.0900 - 1.30 % | Average value: 0.935 % Grade Count:14 |
| Water Absorption at Saturation | 0.400 - 1.20 % @Temperature 45.0 - 400 °C | 0.400 - 1.20 % @Temperature 113 - 752 °F | Average value: 0.814 % Grade Count:2 |
| 0.400 - 1.20 % @Treatment Temp. 70.0 - 70.0 °C | 0.400 - 1.20 % @Treatment Temp. 158 - 158 °F | Average value: 0.814 % Grade Count:2 | |
| Viscosity Measurement | 150 | 150 | Average value: 150 Grade Count:8 |
| Linear Mold Shrinkage | 0.00100 - 0.0100 cm/cm | 0.00100 - 0.0100 in/in | Average value: 0.00310 cm/cm Grade Count:60 |
| Linear Mold Shrinkage, 6.35 mm section | 0.00300 - 0.00700 cm/cm | 0.00300 - 0.00700 in/in | Average value: 0.00445 cm/cm Grade Count:17 |
| Linear Mold Shrinkage, Transverse | 0.00700 - 0.0110 cm/cm | 0.00700 - 0.0110 in/in | Average value: 0.00876 cm/cm Grade Count:21 |
| Melt Flow | 5.00 - 39.3 g/10 min | 5.00 - 39.3 g/10 min | Average value: 31.5 g/10 min Grade Count:9 |
| Spiral Flow | 350 - 450 cm | 138 - 177 in | Average value: 410 cm Grade Count:5 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 117 - 120 | 117 - 120 | Average value: 119 Grade Count:15 |
| Ball Indentation Hardness | 120 - 245 MPa | 17400 - 35500 psi | Average value: 174 MPa Grade Count:7 |
| Tensile Strength, Ultimate | 75.0 - 210 MPa | 10900 - 30500 psi | Average value: 145 MPa Grade Count:71 |
| Tensile Strength, Yield | 140 - 193 MPa | 20300 - 28000 psi | Average value: 164 MPa Grade Count:9 |
| Elongation at Break | 2.00 - 25.0 % | 2.00 - 25.0 % | Average value: 4.92 % Grade Count:65 |
| Elongation at Yield | 2.50 - 6.00 % | 2.50 - 6.00 % | Average value: 3.79 % Grade Count:18 |
| Modulus of Elasticity | 3.50 - 15.5 GPa | 508 - 2250 ksi | Average value: 9.02 GPa Grade Count:65 |
| Flexural Yield Strength | 121 - 290 MPa | 17500 - 42100 psi | Average value: 215 MPa Grade Count:54 |
| Flexural Modulus | 3.45 - 13.1 GPa | 500 - 1900 ksi | Average value: 7.85 GPa Grade Count:58 |
| Compressive Yield Strength | 100 - 179 MPa | 14500 - 26000 psi | Average value: 150 MPa Grade Count:10 |
| Izod Impact, Notched | 0.534 - 1.87 J/cm | 1.00 - 3.50 ft-lb/in | Average value: 1.25 J/cm Grade Count:44 |
| Izod Impact, Unnotched | 4.27 - 13.7 J/cm | 8.00 - 25.7 ft-lb/in | Average value: 9.46 J/cm Grade Count:32 |
| Izod Impact, Notched (ISO) | 9.70 - 17.0 kJ/m2 | 4.62 - 8.09 ft-lb/in2 | Average value: 14.8 kJ/m2 Grade Count:7 |
| Izod Impact, Unnotched (ISO) | 65.0 - 95.0 kJ/m2 | 30.9 - 45.2 ft-lb/in2 | Average value: 78.7 kJ/m2 Grade Count:5 |
| Charpy Impact Unnotched | 7.50 - 11.0 J/cm2 | 35.7 - 52.4 ft-lb/in2 | Average value: 9.16 J/cm2 Grade Count:31 |
| 6.00 - 11.0 J/cm2 @Temperature -30.0 - 30.0 °C | 28.6 - 52.4 ft-lb/in2 @Temperature -22.0 - 86.0 °F | Average value: 8.79 J/cm2 Grade Count:20 | |
| Charpy Impact, Notched | 0.500 - 3.10 J/cm2 | 2.38 - 14.8 ft-lb/in2 | Average value: 1.61 J/cm2 Grade Count:27 |
| 0.500 - 1.80 J/cm2 @Temperature -30.0 - 30.0 °C | 2.38 - 8.57 ft-lb/in2 @Temperature -22.0 - 86.0 °F | Average value: 1.11 J/cm2 Grade Count:20 | |
| Falling Dart Impact | 8.50 - 11.8 J | 6.27 - 8.70 ft-lb | Average value: 9.88 J Grade Count:4 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 460 - 1.00e+16 ohm-cm | 460 - 1.00e+16 ohm-cm | Average value: 8.77e+14 ohm-cm Grade Count:31 |
| Surface Resistance | 1.00e+11 ohm | 1.00e+11 ohm | Average value: 1.00e+11 ohm Grade Count:7 |
| Dielectric Constant | 3.60 - 3.80 | 3.60 - 3.80 | Average value: 3.74 Grade Count:9 |
| Dielectric Strength | 5.00 - 45.0 kV/mm | 127 - 1140 kV/in | Average value: 30.6 kV/mm Grade Count:18 |
| Dissipation Factor | 0.0110 - 0.0160 | 0.0110 - 0.0160 | Average value: 0.0136 Grade Count:8 |
| Arc Resistance | 120 - 130 sec | 120 - 130 sec | Average value: 126 sec Grade Count:6 |
| Comparative Tracking Index | 600 V | 600 V | Average value: 600 V Grade Count:8 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 15.3 - 48.6 μm/m-°C | 8.50 - 27.0 μin/in-°F | Average value: 28.0 μm/m-°C Grade Count:23 |
| CTE, linear, Transverse to Flow | 72.0 - 88.0 μm/m-°C | 40.0 - 48.9 μin/in-°F | Average value: 80.0 μm/m-°C Grade Count:7 |
| Thermal Conductivity | 0.300 - 0.562 W/m-K | 2.08 - 3.90 BTU-in/hr-ft2-°F | Average value: 0.467 W/m-K Grade Count:10 |
| Melting Point | 214 - 260 °C | 418 - 500 °F | Average value: 223 °C Grade Count:31 |
| Maximum Service Temperature, Air | 90.0 - 160 °C | 194 - 320 °F | Average value: 133 °C Grade Count:8 |
| Deflection Temperature at 0.46 MPa (66 psi) | 207 - 224 °C | 405 - 435 °F | Average value: 219 °C Grade Count:27 |
| Deflection Temperature at 1.8 MPa (264 psi) | 190 - 218 °C | 374 - 425 °F | Average value: 208 °C Grade Count:56 |
| Deflection Temperature at 8.0 MPa | 75.0 - 170 °C | 167 - 338 °F | Average value: 134 °C Grade Count:12 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:47 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 265 - 293 °C | 509 - 560 °F | Average value: 283 °C Grade Count:18 |
| Feed Temperature | 60.0 - 230 °C | 140 - 446 °F | Average value: 115 °C Grade Count:7 |
| Nozzle Temperature | 240 - 295 °C | 464 - 563 °F | Average value: 269 °C Grade Count:8 |
| Melt Temperature | 215 - 320 °C | 419 - 608 °F | Average value: 268 °C Grade Count:37 |
| Mold Temperature | 60.0 - 110 °C | 140 - 230 °F | Average value: 86.9 °C Grade Count:52 |
| Drying Temperature | 75.0 - 105 °C | 167 - 221 °F | Average value: 80.8 °C Grade Count:29 |
| Dry Time | 2.00 - 8.00 hour | 2.00 - 8.00 hour | Average value: 3.35 hour Grade Count:20 |
| Moisture Content | 0.0200 - 0.200 % | 0.0200 - 0.200 % | Average value: 0.176 % Grade Count:19 |
| Dew Point | -17.8 °C | 0.000 °F | Average value: -17.8 °C Grade Count:9 |
| Injection Pressure | 68.9 - 130 MPa | 10000 - 18900 psi | Average value: 97.2 MPa Grade Count:32 |
| Hold Pressure | 75.0 MPa | 10900 psi | Average value: 75.0 MPa Grade Count:5 |
| Back Pressure | 0.172 - 1.00 MPa | 24.9 - 145 psi | Average value: 0.504 MPa Grade Count:9 |