- 熔體流動速率 [g/10min]: 4.0
- 密度 [g/cm3]: 1.03
- 吸水率 [%]: 0.1
- 缺口沖擊強度: 0.29
- 拉伸強度 [MPa]: 32.0
- 斷裂伸長率 [%]: 22.0
- 彎曲強度 [MPa]: 0.22
- 彎曲模量 [MPa]: 0.530
- 硬度: 111.0
- 熱變形溫度 [℃]: 65.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.03 - 3.80 g/cc | 0.0372 - 0.137 lb/in3 | Average value: 1.30 g/cc Grade Count:194 |
| Filler Content | 10.0 - 50.0 % | 10.0 - 50.0 % | Average value: 28.2 % Grade Count:46 |
| Water Absorption | 0.100 - 4.00 % | 0.100 - 4.00 % | Average value: 1.14 % Grade Count:95 |
| Moisture Absorption at Equilibrium | 0.0900 - 4.80 % | 0.0900 - 4.80 % | Average value: 0.558 % Grade Count:62 |
| Water Absorption at Saturation | 0.400 - 1.20 % @Temperature 45.0 - 400 °C | 0.400 - 1.20 % @Temperature 113 - 752 °F | Average value: 0.814 % Grade Count:2 |
| 0.400 - 1.20 % @Treatment Temp. 70.0 - 70.0 °C | 0.400 - 1.20 % @Treatment Temp. 158 - 158 °F | Average value: 0.814 % Grade Count:2 | |
| Filament Diameter | 200 - 500 μm | 200 - 500 μm | Average value: 367 μm Grade Count:3 |
| Viscosity | 700 - 5000 cP @Temperature 230 - 230 °C | 700 - 5000 cP @Temperature 446 - 446 °F | Average value: 2230 cP Grade Count:1 |
| 700 - 5000 cP @Shear Rate 10.0 - 1000 1/s | 700 - 5000 cP @Shear Rate 10.0 - 1000 1/s | Average value: 2230 cP Grade Count:1 | |
| Viscosity Measurement | 90.0 - 200 | 90.0 - 200 | Average value: 147 Grade Count:11 |
| Linear Mold Shrinkage | 0.000600 - 0.0300 cm/cm | 0.000600 - 0.0300 in/in | Average value: 0.00597 cm/cm Grade Count:151 |
| Linear Mold Shrinkage, 6.35 mm section | 0.00200 - 0.0200 cm/cm | 0.00200 - 0.0200 in/in | Average value: 0.00564 cm/cm Grade Count:26 |
| Linear Mold Shrinkage, Transverse | 0.00200 - 0.0400 cm/cm | 0.00200 - 0.0400 in/in | Average value: 0.0113 cm/cm Grade Count:76 |
| Melt Flow | 4.00 - 130 g/10 min | 4.00 - 130 g/10 min | Average value: 45.6 g/10 min Grade Count:12 |
| Spiral Flow | 350 - 700 cm | 138 - 276 in | Average value: 458 cm Grade Count:6 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 111 - 122 | 111 - 122 | Average value: 118 Grade Count:20 |
| Ball Indentation Hardness | 35.0 - 245 MPa | 5080 - 35500 psi | Average value: 113 MPa Grade Count:17 |
| Tensile Strength, Ultimate | 0.220 - 524 MPa | 31.9 - 76000 psi | Average value: 100 MPa Grade Count:179 |
| 0.0300 - 94.56 MPa @Temperature -40.0 - 150 °C | 4.35 - 13710 psi @Temperature -40.0 - 302 °F | Average value: 32.7 MPa Grade Count:3 | |
| 0.0300 - 94.56 MPa @Strain 0.000 - 309 % | 4.35 - 13710 psi @Strain 0.000 - 309 % | Average value: 32.7 MPa Grade Count:3 | |
| Tensile Strength, Yield | 32.0 - 237 MPa | 4640 - 34400 psi | Average value: 100 MPa Grade Count:48 |
| Elongation at Break | 0.500 - 258 % | 0.500 - 258 % | Average value: 27.4 % Grade Count:177 |
| Elongation at Yield | 1.50 - 100 % | 1.50 - 100 % | Average value: 7.90 % Grade Count:54 |
| Modulus of Elasticity | 0.450 - 44.2 GPa | 65.3 - 6410 ksi | Average value: 8.15 GPa Grade Count:164 |
| 0.213 - 2.579 GPa @Temperature -40.0 - 150 °C | 30.9 - 374.1 ksi @Temperature -40.0 - 302 °F | Average value: 1.22 GPa Grade Count:2 | |
| Tenacity | 0.370 - 0.509 N/tex | 4.19 - 5.77 g/denier | Average value: 0.447 N/tex Grade Count:3 |
| Flexural Yield Strength | 22.0 - 393 MPa | 3190 - 57000 psi | Average value: 204 MPa Grade Count:138 |
| Flexural Modulus | 0.530 - 22.4 GPa | 76.9 - 3250 ksi | Average value: 7.74 GPa Grade Count:154 |
| Compressive Yield Strength | 68.9 - 179 MPa | 10000 - 26000 psi | Average value: 140 MPa Grade Count:12 |
| Shear Strength | 65.5 - 79.0 MPa | 9500 - 11500 psi | Average value: 72.2 MPa Grade Count:3 |
| Izod Impact, Notched | 0.290 - 6.03 J/cm | 0.543 - 11.3 ft-lb/in | Average value: 1.10 J/cm Grade Count:126 |
| Izod Impact, Unnotched | 3.25 - 5340 J/cm | 6.09 - 10000 ft-lb/in | Average value: 8.41 J/cm Grade Count:87 |
| Izod Impact, Notched (ISO) | 1.00 - 88.2 kJ/m2 | 0.476 - 42.0 ft-lb/in2 | Average value: 15.6 kJ/m2 Grade Count:55 |
| Izod Impact, Unnotched (ISO) | 20.0 - 21000 kJ/m2 | 9.52 - 9990 ft-lb/in2 | Average value: 52.5 kJ/m2 Grade Count:44 |
| Charpy Impact Unnotched | 3.00 - 1000 J/cm2 | 14.3 - 4760 ft-lb/in2 | Average value: 8.92 J/cm2 Grade Count:56 |
| 4.50 - 999.9 J/cm2 @Temperature -30.0 - 30.0 °C | 21.4 - 4759 ft-lb/in2 @Temperature -22.0 - 86.0 °F | Average value: 9.26 J/cm2 Grade Count:37 | |
| Charpy Impact, Notched | 0.370 - 1000 J/cm2 | 1.76 - 4760 ft-lb/in2 | Average value: 2.16 J/cm2 Grade Count:54 |
| 0.300 - 2.10 J/cm2 @Temperature -40.0 - 30.0 °C | 1.43 - 9.99 ft-lb/in2 @Temperature -40.0 - 86.0 °F | Average value: 1.10 J/cm2 Grade Count:40 | |
| Gardner Impact | 4.63 - 36.2 J | 3.42 - 26.7 ft-lb | Average value: 28.3 J Grade Count:4 |
| Dart Drop, Total Energy | 1.00 - 22.0 J | 0.738 - 16.2 ft-lb | Average value: 7.13 J Grade Count:23 |
| Falling Dart Impact | 8.50 - 11.8 J | 6.27 - 8.70 ft-lb | Average value: 9.88 J Grade Count:4 |
| Coefficient of Friction | 0.190 - 0.710 | 0.190 - 0.710 | Average value: 0.421 Grade Count:21 |
| Coefficient of Friction, Static | 0.100 - 0.520 | 0.100 - 0.520 | Average value: 0.326 Grade Count:21 |
| K (wear) Factor | 6.04 - 894 x 10-8 mm3/N-M | 3.00 - 444 x 10-10 in3-min/ft-lb-hr | Average value: 137 x 10-8 mm3/N-M Grade Count:19 |
| Taber Abrasion, mg/1000 Cycles | 6.00 | 6.00 | Average value: 6.00 Grade Count:5 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 5.00 - 1.00e+16 ohm-cm | 5.00 - 1.00e+16 ohm-cm | Average value: 4.43e+14 ohm-cm Grade Count:63 |
| Surface Resistance | 1.00 - 1.00e+14 ohm | 1.00 - 1.00e+14 ohm | Average value: 3.33e+12 ohm Grade Count:31 |
| Dielectric Constant | 3.10 - 3.80 | 3.10 - 3.80 | Average value: 3.65 Grade Count:11 |
| Dielectric Strength | 5.00 - 45.0 kV/mm | 127 - 1140 kV/in | Average value: 32.0 kV/mm Grade Count:29 |
| Dissipation Factor | 0.0110 - 0.0200 | 0.0110 - 0.0200 | Average value: 0.0143 Grade Count:9 |
| Arc Resistance | 120 - 130 sec | 120 - 130 sec | Average value: 125 sec Grade Count:7 |
| Comparative Tracking Index | 600 V | 600 V | Average value: 600 V Grade Count:18 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 1.50 - 200 μm/m-°C | 0.833 - 111 μin/in-°F | Average value: 56.0 μm/m-°C Grade Count:74 |
| CTE, linear, Transverse to Flow | 7.83 - 150 μm/m-°C | 4.35 - 83.3 μin/in-°F | Average value: 81.4 μm/m-°C Grade Count:52 |
| Thermal Conductivity | 0.216 - 0.562 W/m-K | 1.50 - 3.90 BTU-in/hr-ft2-°F | Average value: 0.449 W/m-K Grade Count:12 |
| Melting Point | 208 - 260 °C | 406 - 500 °F | Average value: 221 °C Grade Count:61 |
| Maximum Service Temperature, Air | 80.0 - 160 °C | 176 - 320 °F | Average value: 133 °C Grade Count:19 |
| Deflection Temperature at 0.46 MPa (66 psi) | 65.0 - 232 °C | 149 - 450 °F | Average value: 195 °C Grade Count:94 |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 - 229 °C | 122 - 444 °F | Average value: 170 °C Grade Count:149 |
| Deflection Temperature at 8.0 MPa | 75.0 - 170 °C | 167 - 338 °F | Average value: 134 °C Grade Count:12 |
| Glass Transition Temp, Tg | 70.0 - 73.0 °C | 158 - 163 °F | Average value: 72.0 °C Grade Count:3 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:82 |
| Shrinkage | 2.00 - 18.0 % | 2.00 - 18.0 % | Average value: 8.64 % Grade Count:7 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 265 - 293 °C | 509 - 560 °F | Average value: 282 °C Grade Count:29 |
| Feed Temperature | 60.0 - 230 °C | 140 - 446 °F | Average value: 131 °C Grade Count:10 |
| Nozzle Temperature | 240 - 295 °C | 464 - 563 °F | Average value: 270 °C Grade Count:10 |
| Melt Temperature | 215 - 320 °C | 419 - 608 °F | Average value: 262 °C Grade Count:65 |
| Mold Temperature | 40.0 - 110 °C | 104 - 230 °F | Average value: 84.0 °C Grade Count:84 |
| Drying Temperature | 71.1 - 105 °C | 160 - 221 °F | Average value: 82.0 °C Grade Count:52 |
| Dry Time | 2.00 - 8.00 hour | 2.00 - 8.00 hour | Average value: 3.44 hour Grade Count:38 |
| Moisture Content | 0.0200 - 1.20 % | 0.0200 - 1.20 % | Average value: 0.185 % Grade Count:38 |
| Dew Point | -17.8 °C | 0.000 °F | Average value: -17.8 °C Grade Count:12 |
| Injection Pressure | 68.9 - 130 MPa | 10000 - 18900 psi | Average value: 97.1 MPa Grade Count:46 |
| Hold Pressure | 75.0 MPa | 10900 psi | Average value: 75.0 MPa Grade Count:6 |
| Back Pressure | 0.172 - 1.00 MPa | 24.9 - 145 psi | Average value: 0.499 MPa Grade Count:11 |