- 密度 [g/cm3]: 1.3
- 吸水率 [%]: 0.2
- 缺口沖擊強(qiáng)度: 0.214
- 拉伸強(qiáng)度 [MPa]: 54.5
- 彎曲模量 [MPa]: 2.76
- 熱變形溫度 [℃]: 169.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.30 g/cc | 1.30 g/cc | Method A; ASTM D792 |
| Density | 1.30 g/cc | 0.0470 lb/in3 | ISO 1183 |
| Water Absorption | 0.20 % | 0.20 % | at 24 hrs; ASTM D570 |
| Linear Mold Shrinkage | 0.017 cm/cm | 0.017 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.017 cm/cm | 0.017 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 54.5 MPa | 7900 psi | ASTM D638 |
| Tensile Strength, Yield | 54.5 MPa | 7900 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Elongation at Yield | 3.1 % | 3.1 % | ASTM D638 |
| Tensile Modulus | 3.31 GPa | 480 ksi | ASTM D638 |
| Flexural Strength | 82.7 MPa | 12000 psi | ASTM D790 |
| Flexural Modulus | 2.76 GPa | 400 ksi | ASTM D790 |
| Izod Impact, Notched | 0.214 J/cm @Thickness 3.18 mm | 0.401 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Izod Impact, Unnotched | 2.51 J/cm @Thickness 3.18 mm | 4.70 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Izod Impact, Notched (ISO) | 3.70 kJ/m2 | 1.76 ft-lb/in2 | ISO 180 |
| Izod Impact, Unnotched (ISO) | 16.8 kJ/m2 | 7.99 ft-lb/in2 | ISO 180 |
| Falling Dart Impact | 3.80 J | 2.80 ft-lb | ASTM D3763 |
| Impact Test | 0.970 J | 0.715 ft-lb | Multi-Axial Instrumented Impact Energy; ISO 6603-2 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 169 °C | 336 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 76.7 °C | 170 °F | Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 268 - 274 °C | 514 - 525 °F | |
| Mold Temperature | 65.6 - 93.3 °C | 150 - 200 °F | |
| Drying Temperature | 82.2 °C | 180 °F | |
| Dry Time | 4 hour | 4 hour | |
| Moisture Content | 0.020 % | 0.020 % | Suggested |
| Back Pressure | 0.172 - 0.345 MPa | 24.9 - 50.0 psi | |