- 缺口沖擊強度: 0.32
- 拉伸強度 [MPa]: 79.3
- 彎曲模量 [MPa]: 9.26
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Linear Mold Shrinkage | 0.0090 cm/cm | 0.0090 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.015 cm/cm | 0.015 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 79.3 MPa | 11500 psi | ASTM D638 |
| Tensile Strength, Yield | 79.3 MPa | 11500 psi | ASTM D638 |
| Elongation at Break | 2.1 % | 2.1 % | ASTM D638 |
| Elongation at Yield | 2.1 % | 2.1 % | ASTM D638 |
| Tensile Modulus | 9.98 GPa | 1450 ksi | ASTM D638 |
| Flexural Strength | 145 MPa | 21000 psi | ASTM D790 |
| Flexural Modulus | 9.26 GPa | 1340 ksi | ASTM D790 |
| Izod Impact, Notched | 0.320 J/cm @Thickness 3.18 mm | 0.599 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Izod Impact, Unnotched | 4.22 J/cm @Thickness 3.18 mm | 7.91 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Izod Impact, Notched (ISO) | 4.20 kJ/m2 | 2.00 ft-lb/in2 | ISO 180 |
| Izod Impact, Unnotched (ISO) | 28.1 kJ/m2 | 13.4 ft-lb/in2 | ISO 180 |
| Falling Dart Impact | 8.47 J | 6.25 ft-lb | ASTM D3763 |
| Impact Test | 1.92 J | 1.42 ft-lb | Multi-Axial Instrumented Impact Energy; ISO 6603-2 |
| Thermal Properties | Metric | English | Comments |
| Thermal Conductivity | 1.10 W/m-K | 7.63 BTU-in/hr-ft2-°F | Tested in accordance with ASTM F433; ASTM C177 |
| Deflection Temperature at 1.8 MPa (264 psi) | 168 °C | 334 °F | Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 268 - 274 °C | 514 - 525 °F | |
| Mold Temperature | 65.6 - 93.3 °C | 150 - 200 °F | |
| Drying Temperature | 82.2 °C | 180 °F | |
| Dry Time | 4 hour | 4 hour | |
| Moisture Content | 0.020 % | 0.020 % | Suggested |
| Back Pressure | 0.172 - 0.345 MPa | 24.9 - 50.0 psi | |