- 密度 [g/cm3]: 1.14
- 缺口沖擊強(qiáng)度: 0.48
- 彎曲模量 [MPa]: 3.44
- 熱變形溫度 [℃]: 200.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in3 | ISO 1183 |
| 1.14 g/cc | 0.0412 lb/in3 | ASTM D 792 | |
| Moisture Absorption at Equilibrium | 0.10 % @Time 86400 sec | 0.10 % @Time 24.0 hour | 50% RH; ASTM D 570 |
| Linear Mold Shrinkage, Flow | 0.011 cm/cm @Time 86400 sec | 0.011 in/in @Time 24.0 hour | ISO 294 |
| 0.010 - 0.012 cm/cm @Time 86400 sec | 0.010 - 0.012 in/in @Time 24.0 hour | ASTM D 955 | |
| Linear Mold Shrinkage, Transverse | 0.014 cm/cm @Time 86400 sec | 0.014 in/in @Time 24.0 hour | ISO 294 |
| 0.013 - 0.015 cm/cm @Time 86400 sec | 0.013 - 0.015 in/in @Time 24.0 hour | ASTM D 955 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 74.0 MPa | 10700 psi | ISO 527 |
| 75.0 MPa | 10900 psi | ASTM D 638 | |
| Elongation at Break | 2.0 % | 2.0 % | ASTM D 638 |
| 2.8 % | 2.8 % | ISO 527 | |
| Tensile Modulus | 4.06 GPa | 589 ksi | 1 mm/min; ISO 527 |
| 6.20 GPa | 899 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 103 MPa | 14900 psi | ASTM D 790 |
| 111 MPa | 16100 psi | ISO 178 | |
| Flexural Modulus | 3.44 GPa | 499 ksi | ASTM D 790 |
| 3.60 GPa | 522 ksi | ISO 178 | |
| Izod Impact, Notched | 0.480 J/cm @Temperature 23.0 °C | 0.899 ft-lb/in @Temperature 73.4 °F | ASTM D 256 |
| Izod Impact, Unnotched | 2.77 J/cm @Temperature 23.0 °C | 5.19 ft-lb/in @Temperature 73.4 °F | ASTM D 4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m2 @Temperature 23.0 °C | 1.90 ft-lb/in2 @Temperature 73.4 °F | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 16.0 kJ/m2 @Temperature 23.0 °C | 7.61 ft-lb/in2 @Temperature 73.4 °F | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 86.4 μm/m-°C @Temperature -40.0 - 40.0 °C | 48.0 μin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 87.0 μm/m-°C @Temperature -40.0 - 40.0 °C | 48.3 μin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 57.0 μm/m-°C @Temperature -40.0 - 40.0 °C | 31.7 μin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 |
| 57.6 μm/m-°C @Temperature -40.0 - 40.0 °C | 32.0 μin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 200 °C | 392 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 194 °C @Thickness 3.20 mm | 381 °F @Thickness 0.126 in | unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 179 °C | 354 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 188 °C @Thickness 3.20 mm | 370 °F @Thickness 0.126 in | unannealed; ASTM D 648 | |