- 密度 [g/cm3]: 1.36
- 缺口沖擊強度: 4.0
- 彎曲模量 [MPa]: 3.90
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in3 | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.014 - 0.018 cm/cm | 0.014 - 0.018 in/in | on Tensile Bar; SABIC Method |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 74.0 MPa | 10700 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 3.6 % | 3.6 % | 5 mm/min; ISO 527 |
| Flexural Strength | 103 MPa | 14900 psi | break, 2 mm/min; ISO 178 |
| Flexural Modulus | 3.90 GPa | 566 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m2 | 1.90 ft-lb/in2 | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 15.0 kJ/m2 | 7.14 ft-lb/in2 | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 83.0 μm/m-°C @Temperature 23.0 - 60.0 °C | 46.1 μin/in-°F @Temperature 73.4 - 140 °F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 79.0 μm/m-°C @Temperature 23.0 - 60.0 °C | 43.9 μin/in-°F @Temperature 73.4 - 140 °F | ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 87.0 °C | 189 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |