- 密度 [g/cm3]: 1.07
- 缺口沖擊強度: 0.85
- 彎曲強度 [MPa]: 33.0
- 彎曲模量 [MPa]: 1.30
- 硬度: 100.0
- 熱變形溫度 [℃]: 151.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.07 g/cc | 0.0387 lb/in3 | |
| Linear Mold Shrinkage | 0.013 cm/cm | 0.013 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 100 | 100 | ASTM D785 |
| Tensile Strength, Ultimate | 33.0 MPa | 4790 psi | ASTM D638 |
| Elongation at Break | 41 % | 41 % | ASTM D638 |
| Flexural Strength | 52.0 MPa | 7540 psi | ASTM D790 |
| Flexural Modulus | 1.30 GPa | 189 ksi | ASTM D790 |
| Izod Impact, Notched | 0.850 J/cm | 1.59 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | NB | NB | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 195 - 215 °C | 383 - 419 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 151 °C | 304 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 98.0 °C | 208 °F | ASTM D648 |