- 密度 [g/cm3]: 1.05
- 缺口沖擊強(qiáng)度: 2.67
- 彎曲強(qiáng)度 [MPa]: 41.0
- 彎曲模量 [MPa]: 0.380
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in3 | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 41.0 MPa | 5950 psi | ATSM D638 |
| Elongation at Break | 285 % | 285 % | ASTM D638 |
| Flexural Modulus | 0.380 GPa | 55.1 ksi | ASTM D790 |
| Izod Impact, Notched | 2.67 J/cm | 5.00 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 186 °C | 367 °F | ASTM D3418 |
- 關(guān)鍵詞:
- 供應(yīng)
- PA11
- Ashley Polymers Ashlene? 940H Nylon 11