- 密度 [g/cm3]: 1.04
- 吸水率 [%]: 0.3
- 缺口沖擊強度: 0.4
- 彎曲強度 [MPa]: 59.0
- 彎曲模量 [MPa]: 0.980
- 硬度: 108.0
- 熱變形溫度 [℃]: 150.0
- 脆化溫度 [℃]: -70.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in3 | ASTM D792 |
| Water Absorption | 0.30 % | 0.30 % | ASTM D570 |
| Moisture Absorption at Equilibrium | 1.1 % | 1.1 % | 65% RH; ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 108 | 108 | ASTM D785 |
| Tensile Strength, Ultimate | 59.0 MPa | 8560 psi | ATSM D638 |
| Elongation at Break | 290 % | 290 % | ASTM D638 |
| Flexural Modulus | 0.980 GPa | 142 ksi | ASTM D790 |
| Izod Impact, Notched | 0.400 J/cm | 0.749 ft-lb/in | ASTM D256 |
| 0.260 J/cm @Temperature -40.0 °C | 0.487 ft-lb/in @Temperature -40.0 °F | ASTM D256 | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 186 °C | 367 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 150 °C | 302 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ASTM D648 |
| Brittleness Temperature | <= -70.0 °C | <= -94.0 °F | ASTM D746 |
| Glass Transition Temp, Tg | <= -70.0 °C | <= -94.0 °F | ASTM D746 |