- 密度 [g/cm3]: 3.25
- 缺口沖擊強度: 0.32
- 彎曲強度 [MPa]: 32.0
- 彎曲模量 [MPa]: 10.5
- 熱變形溫度 [℃]: 152.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 3.25 g/cc | 0.117 lb/in3 | ISO 1183 | ||
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | LATI | ||
| Linear Mold Shrinkage, Transverse | 0.0050 cm/cm | 0.0050 in/in | LATI | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 77 | 77 | ASTM D785 | ||
| Tensile Strength, Ultimate | 32.0 MPa | 4640 psi | ISO 527 | ||
| 15.0 MPa @Temperature 120 °C | 2180 psi @Temperature 248 °F | ISO 527 | |||
| 18.0 MPa @Temperature 90.0 °C | 2610 psi @Temperature 194 °F | ISO 527 | |||
| 24.0 MPa @Temperature 60.0 °C | 3480 psi @Temperature 140 °F | ISO 527 | |||
| Flexural Modulus | 10.5 GPa | 1520 ksi | ASTM D790 | ||
| Izod Impact, Notched | 0.320 J/cm @Temperature -40.0 °C | 0.599 ft-lb/in @Temperature -40.0 °F | ASTM D256 | ||
| 0.320 J/cm @Temperature -20.0 °C | 0.599 ft-lb/in @Temperature -4.00 °F | ASTM D256 | |||
| 0.330 J/cm @Temperature 23.0 °C | 0.618 ft-lb/in @Temperature 73.4 °F | ASTM D256 | |||
| Charpy Impact Unnotched | 0.800 J/cm2 @Temperature -40.0 °C | 3.81 ft-lb/in2 @Temperature -40.0 °F | DIN 53453 | ||
| 0.900 J/cm2 @Temperature 23.0 °C | 4.28 ft-lb/in2 @Temperature 73.4 °F | DIN 53453 | |||
| 0.900 J/cm2 @Temperature -20.0 °C | 4.28 ft-lb/in2 @Temperature -4.00 °F | DIN 53453 | |||
| Electrical Properties | Metric | English | Comments | ||
| Surface Resistance | 0.265 ohm | 0.265 ohm | IEC 93 | ||
| Dielectric Strength | 0.200 kV/mm @Thickness 2.00 mm | 5.08 kV/in @Thickness 0.0787 in | IEC 243-1 | ||
| Comparative Tracking Index | 188 V | 188 V | IEC 112 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 152 °C | 306 °F | ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 108 °C | 226 °F | ASTM D648 | ||
| Vicat Softening Point | 160 °C | 320 °F | 50°C/h 50N; ISO 306 | ||
| Flammability, UL94 | HB @Thickness 0.710 mm | HB @Thickness 0.0280 in | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 240 - 260 °C | 464 - 500 °F | |||
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |||
| Drying Temperature | 80.0 - 90.0 °C | 176 - 194 °F | Keep the material always warm in a hopper at 70-80°C. Temperature can be reduced when using vacuum ovens. | ||
| Dry Time | >= 3 hour | >= 3 hour | Drying time can be reduced when using vacuum ovens. | ||
| Descriptive Properties | |||||
| Injection Speed | medium | ||||