- 密度 [g/cm3]: 3.25
- 缺口沖擊強度: 0.31
- 彎曲模量 [MPa]: 10.5
- 熱變形溫度 [℃]: 152.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 3.25 g/cc | 0.117 lb/in3 | ISO 1183 | ||
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | LATI | ||
| Linear Mold Shrinkage, Transverse | 0.0050 cm/cm | 0.0050 in/in | LATI | ||
| Mechanical Properties | Metric | English | Comments | ||
| Flexural Modulus | 10.5 GPa | 1520 ksi | ASTM D790 | ||
| Izod Impact, Notched | 0.310 J/cm @Temperature 23.0 °C | 0.581 ft-lb/in @Temperature 73.4 °F | ASTM D256 | ||
| Electrical Properties | Metric | English | Comments | ||
| Comparative Tracking Index | 295 V | 295 V | IEC 112 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 152 °C | 306 °F | ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | ASTM D648 | ||
| Vicat Softening Point | 165 °C | 329 °F | 50°C/h 50N; ISO 306 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 240 - 260 °C | 464 - 500 °F | |||
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |||
| Drying Temperature | 80.0 - 90.0 °C | 176 - 194 °F | Keep the material always warm in a hopper at 70-80°C. Temperature can be reduced when using vacuum ovens. | ||
| Dry Time | >= 3 hour | >= 3 hour | Drying time can be reduced when using vacuum ovens. | ||
| Descriptive Properties | |||||
| Injection Speed | medium | ||||