- 密度 [g/cm3]: 1.11
- 吸水率 [%]: 1.4
- 拉伸強度 [MPa]: 37.0
- 熱變形溫度 [℃]: 130.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.11 g/cc | 0.0401 lb/in3 | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.50 % @Thickness 1.00 mm, Temperature 23.0 °C | 0.50 % @Thickness 0.0394 in, Temperature 73.4 °F | 50% R.H.; ISO 62 |
| Water Absorption at Saturation | 1.4 % @Thickness 1.00 mm | 1.4 % @Thickness 0.0394 in | ISO 62 |
| Linear Mold Shrinkage | 0.016 cm/cm | 0.016 in/in | 127x12.7x3.2 mm (processing cond. acc. To ISO 1874-2) |
| Linear Mold Shrinkage, Transverse | 0.016 cm/cm | 0.016 in/in | 127x12.7x3.2 mm (processing cond. acc. To ISO 1874-2) |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 35.0 MPa | 5080 psi | ISO 527-1/2 |
| Tensile Strength, Yield | 37.0 MPa | 5370 psi | ISO 527-1/2 |
| Elongation at Break | 45 % | 45 % | ISO 527-1/2 |
| Elongation at Yield | 5.0 % | 5.0 % | ISO 527-1/2 |
| Tensile Modulus | 1.60 GPa | 232 ksi | ISO 527-1/2 |
| Charpy Impact Unnotched | 8.00 J/cm2 @Temperature -30.0 °C | 38.1 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eU |
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ISO 179/1eU | |
| Charpy Impact, Notched | 0.800 J/cm2 @Temperature -30.0 °C | 3.81 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eA |
| 6.00 J/cm2 @Temperature 23.0 °C | 28.6 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 10 ohm-cm | 10 ohm-cm | IEC 60093 |
| Insulation Resistance | 10 ohm | 10 ohm | Isolation Resistance (ROE DIN 43582:1983/VDE 0303 part 3; IEC 60167 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 178 °C | 352 °F | Peak Temperature; ISO 3146, ISO 11357 |
| Deflection Temperature at 0.46 MPa (66 psi) | 130 °C | 266 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | ISO 75 |
| Vicat Softening Point | 140 °C | 284 °F | 50N; ISO 306 |
| 175 °C | 347 °F | 10N; ISO 306 | |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| HB @Thickness 3.20 mm | HB @Thickness 0.126 in | ||