- 密度 [g/cm3]: 1.02
- 拉伸強度 [MPa]: 30.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.02 g/cc | 0.0368 lb/in3 | ISO 1183 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 43.0 MPa | 6240 psi | ISO 527 | ||
| Tensile Strength, Yield | 30.0 MPa @Strain 50.0 % | 4350 psi @Strain 50.0 % | ISO 527 | ||
| Elongation at Break | >= 150 % | >= 150 % | ISO 527 | ||
| Tensile Modulus | 0.400 GPa | 58.0 ksi | 1 mm/min; ISO 527 | ||
| Charpy Impact Unnotched | NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ISO 179/1eU | ||
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 0.700 J/cm2 @Temperature -30.0 °C | 3.33 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eA | ||
| 14.0 J/cm2 @Temperature 23.0 °C | 66.6 ft-lb/in2 @Temperature 73.4 °F | Partial Break; ISO 179/1eA | |||
| Impact | NB | NB | 8x1 mm tube as molded at -40°C; SAE J2260, SAE J844, ISO 7628-2/DIN 73378 | ||
| NB | NB | 8x1 mm tube after 24 h/110°C, at -40°C; SAE J844 | |||
| NB | NB | 8x1 mm tube after 2 h in boiling water, at -40°C; SAE J844 | |||
| Impact Test | NB | NB | 8x1 mm tube as molded 72 h/150°C, at 23°C; ISO 7628-2/DIN 73378 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 172 °C | 342 °F | 2. heating; ISO 3146 | ||
| Descriptive Properties | |||||
| Burst Test Hoop Stress | 24.8 MPA | 8x1 mm tube, DIN 53758 | |||