- 密度 [g/cm3]: 1.01
- 吸水率 [%]: 1.5
- 拉伸強度 [MPa]: 40.0
- 熱變形溫度 [℃]: 115.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.01 g/cc | 0.0365 lb/in3 | ISO 1183 | ||
| Water Absorption | 1.5 % | 1.5 % | ISO 62 | ||
| Moisture Absorption | 0.700 % | 0.700 % | ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.0080 cm/cm | 0.0080 in/in | ISO 294-4, 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in | ISO 294-4, 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 70 | 70 | conditioned, 15s; ISO 868 | ||
| 75 | 75 | dry, 15s; ISO 868 | |||
| Tensile Strength at Break | 50.0 MPa | 7250 psi | dry; ISO 527-1/-2 | ||
| 50.0 MPa | 7250 psi | conditioned; ISO 527-1/-2 | |||
| Tensile Strength, Yield | 40.0 MPa | 5800 psi | dry; ISO 527-1/-2 | ||
| 50.0 MPa | 7250 psi | dry; ISO 527-1/-2 | |||
| Elongation at Break | >= 50 % | >= 50 % | conditioned; ISO 527-1/-2 | ||
| <= 50 % | <= 50 % | dry; ISO 527-1/-2 | |||
| Elongation at Yield | 5.0 % | 5.0 % | dry; ISO 527-1/-2 | ||
| 10 % | 10 % | conditioned; ISO 527-1/-2 | |||
| Tensile Modulus | 1.20 GPa | 174 ksi | conditioned; ISO 527-1/-2 | ||
| 1.60 GPa | 232 ksi | dry; ISO 527-1/-2 | |||
| Charpy Impact Unnotched | NB | NB | dry; ISO 179/1eU | ||
| NB | NB | conditioned; ISO 179/1eU | |||
| NB @Temperature 30.0 °C | NB @Temperature 86.0 °F | dry; ISO 179/1eU | |||
| NB @Temperature 30.0 °C | NB @Temperature 86.0 °F | conditioned; ISO 179/1eU | |||
| Charpy Impact, Notched | 0.600 J/cm2 | 2.86 ft-lb/in2 | dry; ISO 179/1eA | ||
| 0.700 J/cm2 | 3.33 ft-lb/in2 | conditioned; ISO 179/1eA | |||
| 0.600 J/cm2 @Temperature 30.0 °C | 2.86 ft-lb/in2 @Temperature 86.0 °F | dry; ISO 179/1eU | |||
| 0.600 J/cm2 @Temperature 30.0 °C | 2.86 ft-lb/in2 @Temperature 86.0 °F | conditioned; ISO 179/1eU | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | dry; IEC 60093 | ||
| 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | conditioned; IEC 60093 | |||
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 | ||
| Dielectric Strength | 35.0 kV/mm | 889 kV/in | conditioned; IEC 60243-1 | ||
| 36.0 kV/mm | 914 kV/in | dry; IEC 60243-1 | |||
| Comparative Tracking Index | 600 V | 600 V | conditioned; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 120 μm/m-°C | 66.7 μin/in-°F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 140 μm/m-°C | 77.8 μin/in-°F | ISO 11359-1/-2 | ||
| Melting Point | 178 °C | 352 °F | 10°C/min; ISO 11357-1/-3 | ||
| Maximum Service Temperature, Air | 90.0 - 110 °C | 194 - 230 °F | long term; EMS | ||
| 150 °C | 302 °F | short term; EMS | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | ISO 75-1/-2 | ||
| Flammability, UL94 | HB | HB | IEC 60695-11-10 | ||
| Descriptive Properties | |||||
| Automotive | Fuel systems | ||||
| Hydraulic systems | |||||
| Form | Granules | ||||
| Processing | Other Extrusion | ||||
| Special Characteristics | Improved heat resistance | ||||