- 密度 [g/cm3]: 1.04
- 吸水率 [%]: 2.5
- 拉伸強度 [MPa]: 70.0
- 熱變形溫度 [℃]: 90.0
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in3 | ISO 1183 | ||
| Water Absorption | 2.5 % | 2.5 % | ISO 62 | ||
| Moisture Absorption | 1.00 % | 1.00 % | ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | ISO 294-4, 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.0050 cm/cm | 0.0050 in/in | ISO 294-4, 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 110 MPa | 16000 psi | conditioned; ISO 2039-1 | ||
| Tensile Strength at Break | 40.0 MPa | 5800 psi | conditioned; ISO 527-1/-2 | ||
| Tensile Strength, Yield | 70.0 MPa | 10200 psi | conditioned; ISO 527-1/-2 | ||
| Elongation at Break | >= 50 % | >= 50 % | conditioned; ISO 527-1/-2 | ||
| Elongation at Yield | 6.0 % | 6.0 % | conditioned; ISO 527-1/-2 | ||
| Tensile Modulus | 1.90 GPa | 276 ksi | conditioned; ISO 527-1/-2 | ||
| Charpy Impact Unnotched | NB | NB | conditioned; ISO 179/1eU | ||
| NB @Temperature 30.0 °C | NB @Temperature 86.0 °F | conditioned; ISO 179/1eU | |||
| Charpy Impact, Notched | 0.900 J/cm2 | 4.28 ft-lb/in2 | conditioned; ISO 179/1eA | ||
| 0.800 J/cm2 @Temperature 30.0 °C | 3.81 ft-lb/in2 @Temperature 86.0 °F | conditioned; ISO 179/1eU | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | conditioned; IEC 60093 | ||
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 | ||
| Dielectric Strength | 32.0 kV/mm | 813 kV/in | conditioned; IEC 60243-1 | ||
| Comparative Tracking Index | 600 V | 600 V | conditioned; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 90.0 μm/m-°C | 50.0 μin/in-°F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 90.0 μm/m-°C | 50.0 μin/in-°F | ISO 11359-1/-2 | ||
| Maximum Service Temperature, Air | 80.0 °C | 176 °F | long term; EMS | ||
| 95.0 °C | 203 °F | short term; EMS | |||
| Transformation Temperature, Tg | 110 °C | 230 °F | 10°C/min; ISO 11357-1/-2 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 90.0 °C | 194 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | ISO 75-1/-2 | ||
| Flammability, UL94 | HB | HB | IEC 60695-11-10 | ||
| Optical Properties | Metric | English | Comments | ||
| Transmission, Visible | 90.0 % | 90.0 % | transparent; thickness not quantified | ||
| Descriptive Properties | |||||
| Automotive | Cooling and climate control | ||||
| Fuel systems | |||||
| Powertrain and Chassis | |||||
| Form | Granules | ||||
| Industry & Consumer goods | Housewares | ||||
| Mechanical Engineering | |||||
| Sports & Leisure | |||||
| Tools & Accessories | |||||
| Optics | Optical components | ||||
| Spectacle frames | |||||
| Sunglasses | |||||
| Processing | Injection Molding | ||||
| Product Attributes | Improved alcohol resistance | ||||
| Special Characteristics | Transparent | ||||
| Water Contact | NSF 61 | ||||