- 熔體流動速率 [g/10min]: 1.1
- 密度 [g/cm3]: 1.41
- 彎曲強度 [MPa]: 150.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in3 | |
| Melt Flow | 1.1 g/10 min @Load 2.16 kg, Temperature 235 °C | 1.1 g/10 min @Load 4.76 lb, Temperature 455 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 150 MPa | 21800 psi | 5 mm/min |
| Elongation at Break | 4.0 % | 4.0 % | 5 mm/min |
| Tensile Modulus | 15.9 GPa | 2310 ksi | 1 mm/min |
| Charpy Impact Unnotched | 8.95 J/cm2 | 42.6 ft-lb/in2 | |
| 8.75 J/cm2 @Temperature -30.0 °C | 41.6 ft-lb/in2 @Temperature -22.0 °F | ||
| Charpy Impact, Notched | 2.32 J/cm2 | 11.0 ft-lb/in2 | |
| 1.76 J/cm2 @Temperature -30.0 °C | 8.38 ft-lb/in2 @Temperature -22.0 °F | ||