- 熔體流動速率 [g/10min]: 4.6
- 密度 [g/cm3]: 1.1
- 彎曲強度 [MPa]: 128.0
- 熱變形溫度 [℃]: 175.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in3 | |
| Melt Flow | 4.6 g/10 min @Load 2.16 kg, Temperature 235 °C | 4.6 g/10 min @Load 4.76 lb, Temperature 455 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 128 MPa | 18600 psi | 5 mm/min |
| Elongation at Break | 4.0 % | 4.0 % | 5 mm/min |
| Tensile Modulus | 11.4 GPa | 1650 ksi | 1 mm/min |
| Charpy Impact Unnotched | 6.37 J/cm2 | 30.3 ft-lb/in2 | |
| 5.83 J/cm2 @Temperature -30.0 °C | 27.7 ft-lb/in2 @Temperature -22.0 °F | ||
| Charpy Impact, Notched | 1.73 J/cm2 | 8.23 ft-lb/in2 | |
| 1.00 J/cm2 @Temperature -30.0 °C | 4.76 ft-lb/in2 @Temperature -22.0 °F | ||
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 600 ohm-cm | 600 ohm-cm | |
| Dielectric Strength | 1.00 kV/mm | 25.4 kV/in | |
| Comparative Tracking Index | 100 V | 100 V | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 40.0 μm/m-°C @Temperature 20.0 °C | 22.2 μin/in-°F @Temperature 68.0 °F | |
| Melting Point | 174 °C | 345 °F | (Dry) |
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C | 347 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 160 °C | 320 °F | |
| Vicat Softening Point | 170 °C | 338 °F | 50°C/hr; 50N |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| HB @Thickness 3.10 mm | HB @Thickness 0.122 in | ||