- 熔體流動速率 [g/10min]: 12.9
- 彎曲強度 [MPa]: 72.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Flow | 12.9 g/10 min @Load 2.16 kg, Temperature 235 °C | 12.9 g/10 min @Load 4.76 lb, Temperature 455 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 72.0 MPa | 10400 psi | 5 mm/min |
| Elongation at Break | 8.0 % | 8.0 % | 5 mm/min |
| Tensile Modulus | 3.83 GPa | 556 ksi | 1 mm/min |
| Charpy Impact Unnotched | 6.40 J/cm2 | 30.5 ft-lb/in2 | |
| 6.87 J/cm2 @Temperature -30.0 °C | 32.7 ft-lb/in2 @Temperature -22.0 °F | ||
| Charpy Impact, Notched | 1.15 J/cm2 | 5.47 ft-lb/in2 | |
| 0.720 J/cm2 @Temperature -30.0 °C | 3.43 ft-lb/in2 @Temperature -22.0 °F | ||
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 151 °C | 304 °F | 50°C/hr; 50N |