- 熔體流動速率 [g/10min]: 2.1
- 密度 [g/cm3]: 1.07
- 拉伸強度 [MPa]: 45.0
- 熱變形溫度 [℃]: 162.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.07 g/cc | 0.0387 lb/in3 | |
| Melt Flow | 2.1 g/10 min @Load 2.16 kg, Temperature 235 °C | 2.1 g/10 min @Load 4.76 lb, Temperature 455 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 45.0 MPa | 6530 psi | 50 mm/min |
| Elongation at Break | >= 50 % | >= 50 % | Nominal Strain; 50 mm/min |
| Elongation at Yield | 7.0 % | 7.0 % | 50 mm/min |
| Tensile Modulus | 2.20 GPa | 319 ksi | 1 mm/min |
| Charpy Impact Unnotched | 13.3 J/cm2 | 63.3 ft-lb/in2 | |
| 11.1 J/cm2 @Temperature -30.0 °C | 52.8 ft-lb/in2 @Temperature -22.0 °F | ||
| Charpy Impact, Notched | 0.450 J/cm2 | 2.14 ft-lb/in2 | |
| 0.420 J/cm2 @Temperature -30.0 °C | 2.00 ft-lb/in2 @Temperature -22.0 °F | ||
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 80.0 μm/m-°C @Temperature 20.0 °C | 44.4 μin/in-°F @Temperature 68.0 °F | |
| Melting Point | 174 °C | 345 °F | (Dry) |
| Deflection Temperature at 0.46 MPa (66 psi) | 162 °C | 324 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | |
| Flammability, UL94 | V-2 @Thickness 1.60 mm | V-2 @Thickness 0.0630 in | |
| V-2 @Thickness 3.20 mm | V-2 @Thickness 0.126 in | ||