- 密度 [g/cm3]: 1.66
- 吸水率 [%]: 3.6
- 彎曲模量 [MPa]: 16.5
- 熱變形溫度 [℃]: 220.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.66 g/cc | 0.0600 lb/in3 | ISO 1183 | ||
| Water Absorption | 3.6 % | 3.6 % | Sim. to ISO 62 | ||
| Moisture Absorption at Equilibrium | 1.0 % | 1.0 % | Humidity Absorption; Sim. to ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm | 0.0020 in/in | Parallel; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in | Normal; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 235 MPa | 34100 psi | ISO 527-1/-2 | ||
| Elongation at Break | 2.2 % | 2.2 % | ISO 527-1/-2 | ||
| Tensile Modulus | 20.0 GPa | 2900 ksi | ISO 527-1/-2 | ||
| Flexural Strength | 360 MPa | 52200 psi | ISO 178 | ||
| Flexural Modulus | 16.5 GPa | 2390 ksi | ISO 178 | ||
| Charpy Impact Unnotched | 8.50 J/cm2 @Temperature -30.0 °C | 40.5 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eU | ||
| 9.00 J/cm2 @Temperature 23.0 °C | 42.8 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 1.20 J/cm2 @Temperature -30.0 °C | 5.71 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eA | ||
| 1.50 J/cm2 @Temperature 23.0 °C | 7.14 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 10.0 μm/m-°C @Temperature 20.0 °C | 5.56 μin/in-°F @Temperature 68.0 °F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 40.0 μm/m-°C @Temperature 20.0 °C | 22.2 μin/in-°F @Temperature 68.0 °F | ISO 11359-1/-2 | ||
| Melting Point | 220 °C | 428 °F | 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ISO 75-1/-2 | ||
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | IEC 60695-11-10 | ||
| Descriptive Properties | |||||
| Injection Molding | Yes | ||||
| With Fillers | Yes | ||||