- 密度 [g/cm3]: 1.13
- 吸水率 [%]: 9.0
- 拉伸強(qiáng)度 [MPa]: 95.0
- 熱變形溫度 [℃]: 190.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in3 | ISO 1183 | ||
| Water Absorption | 9.0 % | 9.0 % | Sim. to ISO 62 | ||
| Moisture Absorption at Equilibrium | 2.5 % | 2.5 % | Humidity Absorption; Sim. to ISO 62 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 95.0 MPa | 13800 psi | ISO 527-1/-2 | ||
| Elongation at Break | 15 % | 15 % | ISO 527-1/-2 | ||
| Elongation at Yield | 3.5 % | 3.5 % | ISO 527-1/-2 | ||
| Tensile Modulus | 3.80 GPa | 551 ksi | ISO 527-1/-2 | ||
| Charpy Impact Unnotched | NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ISO 179/1eU | ||
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 0.400 J/cm2 @Temperature -30.0 °C | 1.90 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eA | ||
| 0.800 J/cm2 @Temperature 23.0 °C | 3.81 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 | ||
| Dielectric Constant | 3.0 @Frequency 1e+6 Hz | 3.0 @Frequency 1e+6 Hz | IEC 60250 | ||
| 3.2 @Frequency 100 Hz | 3.2 @Frequency 100 Hz | IEC 60250 | |||
| Dielectric Strength | 25.0 kV/mm | 635 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.0050 @Frequency 100 Hz | 0.0050 @Frequency 100 Hz | IEC 60250 | ||
| 0.015 @Frequency 1e+6 Hz | 0.015 @Frequency 1e+6 Hz | IEC 60250 | |||
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 90.0 μm/m-°C @Temperature 20.0 °C | 50.0 μin/in-°F @Temperature 68.0 °F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 90.0 μm/m-°C @Temperature 20.0 °C | 50.0 μin/in-°F @Temperature 68.0 °F | ISO 11359-1/-2 | ||
| Melting Point | 220 °C | 428 °F | 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 190 °C | 374 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | ISO 75-1/-2 | ||
| Vicat Softening Point | 195 °C | 383 °F | 50°C/h 50N; ISO 306 | ||
| Flammability, UL94 | V-2 @Thickness 1.60 mm | V-2 @Thickness 0.0630 in | IEC 60695-11-10 | ||
| V-2 @Thickness 3.00 mm | V-2 @Thickness 0.118 in | IEC 60695-11-10 | |||
| Oxygen Index | 26 % | 26 % | ISO 4589-1/-2 | ||
| Descriptive Properties | |||||
| Injection Molding | Yes | ||||
| Release agent | Yes | ||||
| Without fillers | Yes | ||||