- 密度 [g/cm3]: 1.47
- 吸水率 [%]: 0.9
- 缺口沖擊強度: 0.5
- 彎曲強度 [MPa]: 86.2
- 彎曲模量 [MPa]: 5.20
- 硬度: 122.0
- 熱變形溫度 [℃]: 182.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.47 g/cc | 0.0531 lb/in3 | ASTM D792 |
| Water Absorption | 0.90 % | 0.90 % | 24 hour immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.010 cm/cm | 0.010 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 95 | 95 | ASTM D785 |
| Hardness, Rockwell R | 122 | 122 | ASTM D785 |
| Tensile Strength, Ultimate | 86.2 MPa | 12500 psi | ASTM D638 |
| Elongation at Break | 12.5 % | 12.5 % | ASTM D638 |
| Flexural Strength | 124 MPa | 18000 psi | ASTM D790 |
| Flexural Modulus | 5.20 GPa | 754 ksi | ASTM D790 |
| Compressive Yield Strength | 186 MPa | 27000 psi | ASTM D695 |
| Izod Impact, Notched | 0.500 J/cm | 0.937 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 222 °C | 432 °F | ASTM D789 |
| Deflection Temperature at 0.46 MPa (66 psi) | 182 °C | 360 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 143 °C | 289 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | |