- 密度 [g/cm3]: 1.47
- 吸水率 [%]: 1.2
- 缺口沖擊強度: 0.4
- 彎曲強度 [MPa]: 137.0
- 彎曲模量 [MPa]: 7.60
- 硬度: 121.0
- 熱變形溫度 [℃]: 216.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.47 g/cc | 0.0531 lb/in3 | ASTM D792 |
| Water Absorption | 1.2 % | 1.2 % | 24 hour immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0055 cm/cm | 0.0055 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 90 | 90 | ASTM D785 |
| Hardness, Rockwell R | 121 | 121 | ASTM D785 |
| Tensile Strength, Ultimate | 137 MPa | 19900 psi | ASTM D638 |
| Elongation at Break | 2.5 % | 2.5 % | ASTM D638 |
| Flexural Strength | 186 MPa | 27000 psi | ASTM D790 |
| Flexural Modulus | 7.60 GPa | 1100 ksi | ASTM D790 |
| Compressive Yield Strength | 159 MPa | 23100 psi | ASTM D695 |
| Izod Impact, Notched | 0.400 J/cm | 0.749 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 222 °C | 432 °F | ASTM D789 |
| Deflection Temperature at 0.46 MPa (66 psi) | 216 °C | 421 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 204 °C | 399 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | |