- 密度 [g/cm3]: 1.13
- 吸水率 [%]: 1.8
- 缺口沖擊強度: 0.6
- 彎曲強度 [MPa]: 75.8
- 彎曲模量 [MPa]: 2.70
- 硬度: 118.0
- 熱變形溫度 [℃]: 182.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in3 | ASTM D792 |
| Water Absorption | 1.8 % | 1.8 % | 24 hour immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0125 cm/cm | 0.0125 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 78 | 78 | ASTM D785 |
| Hardness, Rockwell R | 118 | 118 | ASTM D785 |
| Tensile Strength, Ultimate | 75.8 MPa | 11000 psi | ASTM D638 |
| Elongation at Break | 60 % | 60 % | ASTM D638 |
| Flexural Strength | 103 MPa | 14900 psi | ASTM D790 |
| Flexural Modulus | 2.70 GPa | 392 ksi | ASTM D790 |
| Compressive Yield Strength | 62.0 MPa | 8990 psi | ASTM D695 |
| Izod Impact, Notched | 0.600 J/cm | 1.12 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 222 °C | 432 °F | ASTM D789 |
| Deflection Temperature at 0.46 MPa (66 psi) | 182 °C | 360 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | ASTM D648 |
| Flammability, UL94 | V-2 | V-2 | |