- 熔體流動速率 [g/10min]: 79.0
- 密度 [g/cm3]: 1.12
- 拉伸強度 [MPa]: 84.0
- 斷裂伸長率 [%]: 111
- 彎曲強度 [MPa]: 80.0
- 熱變形溫度 [℃]: 185.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.12 - 1.14 g/cc | 0.0405 - 0.0412 lb/in3 | ASTM D792 | ||
| Apparent Bulk Density | 0.650 g/cc | 0.0235 lb/in3 | circa | ||
| Viscosity Measurement | 2.3 - 2.4 | 2.3 - 2.4 | Relative Viscosity | ||
| Melt Flow | 79 g/10 min @Load 2.16 kg, Temperature 230 °C | 79 g/10 min @Load 4.76 lb, Temperature 446 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Ultimate | 80.0 MPa | 11600 psi | ASTM D638 | ||
| Tensile Strength, Yield | 84.0 MPa | 12200 psi | ASTM D638 | ||
| Elongation at Break | 55 % | 55 % | ASTM D638 | ||
| Elongation at Yield | 3.6 % | 3.6 % | ASTM D638 | ||
| Flexural Yield Strength | 111 MPa | 16100 psi | ASTM D790 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 220 °C | 428 °F | ASTM DSC | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 185 °C | 365 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Moisture Content | <= 0.10 % | <= 0.10 % | |||
| Descriptive Properties | |||||
| Extractables, wt% | <0.5 | ||||