- 熔體流動(dòng)速率 [g/10min]: 40.0
- 密度 [g/cm3]: 1.1
- 缺口沖擊強(qiáng)度: 0.1
- 拉伸強(qiáng)度 [MPa]: 60.0
- 彎曲模量 [MPa]: 2.60
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in3 | ISO 1183 |
| Linear Mold Shrinkage | 0.0030 - 0.0060 cm/cm | 0.0030 - 0.0060 in/in | ISO 2577 |
| Melt Flow | 40 g/10 min @Load 10.0 kg, Temperature 240 °C | 40 g/10 min @Load 22.0 lb, Temperature 464 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | ISO 527 |
| Elongation at Break | 5.0 % | 5.0 % | ISO 527 |
| Tensile Modulus | 3.00 GPa | 435 ksi | ISO 527 |
| Flexural Modulus | 2.60 GPa | 377 ksi | ISO 178 |
| Izod Impact, Notched | 0.100 J/cm @Temperature 23.0 °C | 0.187 ft-lb/in @Temperature 73.4 °F | ISO 180/A |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 135 °C @Load 5.00 kg | 275 °F @Load 11.0 lb | 50°C/hr; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| HB @Thickness 3.20 mm | HB @Thickness 0.126 in | ||