- 熔體流動速率 [g/10min]: 50.0
- 密度 [g/cm3]: 1.07
- 缺口沖擊強度: 0.6
- 拉伸強度 [MPa]: 40.0
- 彎曲模量 [MPa]: 1.90
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.07 g/cc | 0.0387 lb/in3 | ISO 1183 |
| Linear Mold Shrinkage | 0.0050 - 0.0090 cm/cm | 0.0050 - 0.0090 in/in | ISO 2577 |
| Melt Flow | >= 50 g/10 min @Load 10.0 kg, Temperature 240 °C | >= 50 g/10 min @Load 22.0 lb, Temperature 464 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 36.0 MPa | 5220 psi | ISO 527 |
| Tensile Strength, Yield | 40.0 MPa | 5800 psi | ISO 527 |
| Elongation at Break | >= 60 % | >= 60 % | ISO 527 |
| Tensile Modulus | 2.00 GPa | 290 ksi | ISO 527 |
| Flexural Modulus | 1.90 GPa | 276 ksi | ISO 178 |
| Izod Impact, Notched | 0.600 J/cm @Temperature 23.0 °C | 1.12 ft-lb/in @Temperature 73.4 °F | ISO 180/A |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 123 °C @Load 5.00 kg | 253 °F @Load 11.0 lb | 50°C/hr; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| HB @Thickness 3.20 mm | HB @Thickness 0.126 in | ||