- 缺口沖擊強(qiáng)度: 0.961
- 拉伸強(qiáng)度 [MPa]: 38.6
- 彎曲模量 [MPa]: 1.10
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.03 g/cc | 1.03 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.018 cm/cm | 0.018 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 38.6 MPa | 5600 psi | ASTM D638 |
| Flexural Modulus | 1.10 GPa | 160 ksi | ASTM D790 |
| Izod Impact, Notched | 0.961 J/cm @Temperature 22.8 °C | 1.80 ft-lb/in @Temperature 73.0 °F | ASTM D256 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 227 - 254 °C | 440 - 490 °F | |
| Mold Temperature | 65.6 - 93.3 °C | 150 - 200 °F | |
| Dry Time | 2 - 4 hour @Temperature 71.1 °C | 2 - 4 hour @Temperature 160 °F | to ensure moisture content is less than 0.2% |
| Injection Pressure | 4.96 - 8.27 MPa | 720 - 1200 psi | Secondary |
| 8.27 - 13.8 MPa | 1200 - 2000 psi | Initial | |
| Back Pressure | 0.345 - 1.72 MPa | 50.0 - 250 psi | |
| Shot Size | 30 - 80 % | 30 - 80 % | |
| Screw Speed | 20 - 100 rpm | 20 - 100 rpm | |
- 關(guān)鍵詞:
- 供應(yīng)
- PA6
- Clariant Renol PA2SP0004 Nylon 6 Alloy