- 缺口沖擊強度: 0.801
- 拉伸強度 [MPa]: 72.4
- 斷裂伸長率 [%]: 103
- 彎曲模量 [MPa]: 4.14
- 熱變形溫度 [℃]: 199.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Filler Content | 13 % | 13 % | ASTM D2584 |
| Linear Mold Shrinkage, Flow | 0.0060 cm/cm | 0.0060 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 72.4 MPa | 10500 psi | ASTM D638 |
| Elongation at Yield | 4.0 % | 4.0 % | ASTM D638 |
| Flexural Yield Strength | 103 MPa | 15000 psi | ASTM D790 |
| Flexural Modulus | 4.14 GPa | 600 ksi | ASTM D790 |
| Izod Impact, Notched | 0.801 J/cm @Temperature 22.8 °C | 1.50 ft-lb/in @Temperature 73.0 °F | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 199 °C | 390 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 188 °C | 370 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 249 - 266 °C | 480 - 510 °F | |
| Middle Barrel Temperature | 249 - 266 °C | 480 - 510 °F | |
| Front Barrel Temperature | 254 - 271 °C | 490 - 520 °F | |
| Nozzle Temperature | 254 - 274 °C | 490 - 525 °F | |
| Melt Temperature | 254 - 271 °C | 490 - 520 °F | |
| Mold Temperature | 79.4 - 121 °C | 175 - 250 °F | |
| Dry Time | 2 - 4 hour @Temperature 79.4 °C | 2 - 4 hour @Temperature 175 °F | to ensure moisture content of 0.2% or less |
| Injection Pressure | 4.96 - 8.27 MPa | 720 - 1200 psi | Secondary |
| 8.27 - 13.8 MPa | 1200 - 2000 psi | Initial | |
| Back Pressure | 0.345 MPa | 50.0 psi | |
| Shot Size | 30 - 80 % | 30 - 80 % | |
| Screw Speed | 20 - 100 rpm | 20 - 100 rpm | |