- 密度 [g/cm3]: 1.45
- 缺口沖擊強(qiáng)度: 1.2
- 斷裂伸長(zhǎng)率 [%]: 124
- 彎曲強(qiáng)度 [MPa]: 88.0
- 彎曲模量 [MPa]: 3.80
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.45 g/cc | 0.0524 lb/in3 | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 88.0 MPa | 12800 psi | ASTM D638 |
| Elongation at Break | 7.0 % | 7.0 % | ASTM D638 |
| Flexural Yield Strength | 124 MPa | 18000 psi | ASTM D790 |
| Flexural Modulus | 3.80 GPa | 551 ksi | ASTM D790 |
| Izod Impact, Notched | 1.20 J/cm | 2.25 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Flammability, UL94 | V-0 | V-0 | 1/16 in. |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 246 °C | 475 °F | |