- 密度 [g/cm3]: 1.1
- 缺口沖擊強(qiáng)度: 1.6
- 斷裂伸長(zhǎng)率 [%]: 86.0
- 彎曲強(qiáng)度 [MPa]: 62.0
- 彎曲模量 [MPa]: 2.20
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in3 | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 62.0 MPa | 8990 psi | ASTM D638 |
| Elongation at Break | 50 % | 50 % | ASTM D638 |
| Flexural Yield Strength | 86.0 MPa | 12500 psi | ASTM D790 |
| Flexural Modulus | 2.20 GPa | 319 ksi | ASTM D790 |
| Izod Impact, Notched | 1.60 J/cm | 3.00 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 210 °C | 410 °F | ASTM D789 |
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 252 °C | 486 °F | |