- 密度 [g/cm3]: 1.13
- 吸水率 [%]: 1.8
- 缺口沖擊強度: 0.374
- 彎曲模量 [MPa]: 2.90
- 硬度: 120.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in3 | ASTM D792 |
| Water Absorption | 1.8 % | 1.8 % | At 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.010 - 0.014 cm/cm | 0.010 - 0.014 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength at Break | 75.8 MPa | 11000 psi | ASTM D638 |
| Elongation at Break | 55 % | 55 % | ASTM D638 |
| Flexural Strength | 89.6 MPa | 13000 psi | ASTM D790 |
| Flexural Modulus | 2.90 GPa | 420 ksi | ASTM D790 |
| Izod Impact, Notched | 0.374 J/cm | 0.700 ft-lb/in | 0.125 in; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 216 °C | 420 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.6 °C | 150 °F | Unannealed; ASTM D648 |