- 密度 [g/cm3]: 1.06
- 拉伸強(qiáng)度 [MPa]: 50.0
- 彎曲模量 [MPa]: 1.69
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.06 g/cc | 0.0383 lb/in3 | ASTM D792 | ||
| Moisture Absorption at Equilibrium | 2.1 % | 2.1 % | 50% RH; ASTM D570 | ||
| 7.3 % | 7.3 % | Saturation; ASTM D570 | |||
| Linear Mold Shrinkage | 0.04572 cm/cm | 0.04572 in/in | 1/8" bar | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 45.0 MPa | 6530 psi | ASTM D638 | ||
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | ASTM D638 | ||
| Elongation at Break | >= 100 % | >= 100 % | ASTM D638 | ||
| Elongation at Yield | 5.0 % | 5.0 % | ASTM D638 | ||
| Flexural Strength | 65.0 MPa | 9430 psi | ASTM D790 | ||
| Flexural Modulus | 1.69 GPa | 245 ksi | ASTM D790 | ||
| Izod Impact, Notched (ISO) | NB @Temperature -40.0 °C | NB @Temperature -40.0 °F | ASTM D256 | ||
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ASTM D256 | |||
| Dart Drop, Total Energy | 264 J | 195 ft-lb | BASF | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 220 °C | 428 °F | ASTM D3418 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | ASTM D648 | ||
| UL RTI, Electrical | 65.0 °C @Thickness 1.50 mm | 149 °F @Thickness 0.0591 in | 746B | ||
| UL RTI, Mechanical with Impact | 65.0 °C @Thickness 1.50 mm | 149 °F @Thickness 0.0591 in | 746B | ||
| UL RTI, Mechanical without Impact | 65.0 °C @Thickness 1.50 mm | 149 °F @Thickness 0.0591 in | 746B | ||
| Flammability, UL94 | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 270 - 300 °C | 518 - 572 °F | |||
| Mold Temperature | 60.0 - 85.0 °C | 140 - 185 °F | |||
| Dry Time | 2 - 4 hour | 2 - 4 hour | |||
| Moisture Content | <= 0.15 % | <= 0.15 % | |||
| Descriptive Properties | |||||
| Commercial Status | North America | ||||