- 密度 [g/cm3]: 1.36
- 缺口沖擊強度: 182.0
- 彎曲模量 [MPa]: 7.99
- 硬度: 121.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in3 | ASTM D792 | ||
| Moisture Absorption at Equilibrium | 0.90 % | 0.90 % | 24 hour; ASTM D570 | ||
| 1.5 % | 1.5 % | 50% RH; ASTM D570 | |||
| 5.5 % | 5.5 % | Saturation; ASTM D570 | |||
| Linear Mold Shrinkage | 0.00762 cm/cm | 0.00762 in/in | 1/8" bar | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 121 | 121 | |||
| Tensile Strength at Break | 145 MPa | 21000 psi | ASTM D638 | ||
| Elongation at Break | 2.5 % | 2.5 % | ASTM D638 | ||
| Flexural Strength | 232 MPa | 33600 psi | ISO 790 | ||
| Flexural Modulus | 7.99 GPa | 1160 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 182 kJ/m2 | 86.6 ft-lb/in2 | ISO 3146 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 220 °C | 428 °F | ASTM D3418 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 208 °C | 406 °F | ASTM D648 | ||
| Processing Properties | Metric | English | Comments | ||
| Zone 1 | 245 - 275 °C | 473 - 527 °F | Rear Zone | ||
| Zone 2 | 260 - 285 °C | 500 - 545 °F | Center Zone | ||
| Zone 3 | 270 - 295 °C | 518 - 563 °F | Front Zone | ||
| Zone 4 | 270 - 295 °C | 518 - 563 °F | Nozzle | ||
| Melt Temperature | 270 - 295 °C | 518 - 563 °F | |||
| Mold Temperature | 80.0 - 95.0 °C | 176 - 203 °F | |||
| Dry Time | 2 - 4 hour | 2 - 4 hour | |||
| Moisture Content | <= 0.080 % | <= 0.080 % | |||
| Descriptive Properties | |||||
| Color | BK 106 | ||||
| Commercial Status | North America | ||||