- 密度 [g/cm3]: 1.37
- 缺口沖擊強(qiáng)度: 2.25
- 彎曲強(qiáng)度 [MPa]: 170.0
- 彎曲模量 [MPa]: 8.40
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in3 | ISO 1183 | ||
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 170 MPa | 24700 psi | 0.2 in/min; ASTM Test | ||
| 77.0 MPa @Temperature 120 °C | 11200 psi @Temperature 248 °F | ISO Data | |||
| 77.0 MPa @Temperature 120 °C | 11200 psi @Temperature 248 °F | ASTM Test | |||
| 97.0 MPa @Temperature 80.0 °C | 14100 psi @Temperature 176 °F | ASTM Test | |||
| 97.0 MPa @Temperature 80.0 °C | 14100 psi @Temperature 176 °F | ISO Data | |||
| 251 MPa @Temperature -40.0 °C | 36400 psi @Temperature -40.0 °F | ASTM Test | |||
| 251 MPa @Temperature -40.0 °C | 36400 psi @Temperature -40.0 °F | ISO Data | |||
| Tensile Strength, Ultimate | 170 MPa | 24700 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 3.3 % | 3.3 % | 5mm/min; ISO 527 | ||
| 3.3 % | 3.3 % | 0.2 in/min; ASTM Test | |||
| 3.9 % @Temperature -40.0 °C | 3.9 % @Temperature -40.0 °F | ASTM Test | |||
| 3.9 % @Temperature -40.0 °C | 3.9 % @Temperature -40.0 °F | ISO Data | |||
| 6.7 % @Temperature 80.0 °C | 6.7 % @Temperature 176 °F | ASTM Test | |||
| 6.7 % @Temperature 80.0 °C | 6.7 % @Temperature 176 °F | ISO Data | |||
| 7.0 % @Temperature 120 °C | 7.0 % @Temperature 248 °F | ASTM Test | |||
| 7.0 % @Temperature 120 °C | 7.0 % @Temperature 248 °F | ISO Data | |||
| Flexural Strength | 260 MPa | 37700 psi | ASTM Test | ||
| Flexural Modulus | 8.40 GPa | 1220 ksi | ISO Data | ||
| 8.97 GPa | 1300 ksi | ASTM Test | |||
| Izod Impact, Notched | 2.25 J/cm @Thickness 3.17 mm | 4.22 ft-lb/in @Thickness 0.125 in | ASTM Test | ||
| Izod Impact, Notched (ISO) | 26.0 kJ/m2 | 12.4 ft-lb/in2 | ISO Test | ||
| 18.0 kJ/m2 @Temperature -40.0 °C | 8.57 ft-lb/in2 @Temperature -40.0 °F | ISO Test | |||
| Charpy Impact, Notched | 2.30 J/cm2 | 10.9 ft-lb/in2 | ISO 179 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| 220 °C | 428 °F | ASTM Test | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 203 °C | 397 °F | ISO 75 | ||
| 212 °C | 414 °F | ASTM Test | |||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Commercial Status | Active America | ||||
| Impact Modified | Yes | ||||
| Primary Processing Technique | Injection Molding | ||||