- 密度 [g/cm3]: 1.06
- 吸水率 [%]: 6.8
- 缺口沖擊強度: 5.9
- 拉伸強度 [MPa]: 45.0
- 彎曲模量 [MPa]: 1.45
- 硬度: 80.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.06 g/cc | 0.0383 lb/in3 | ISO 1183 | ||
| Water Absorption | 6.8 % | 6.8 % | ISO 62 | ||
| Moisture Absorption at Equilibrium | 1.9 % | 1.9 % | 23°C/50% R.H.; ISO 62 | ||
| Linear Mold Shrinkage | 0.013 cm/cm | 0.013 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 80 | 80 | ASTM Test | ||
| Tensile Strength, Yield | 45.0 MPa | 6530 psi | 50mm/min; ISO 527 | ||
| 50.0 MPa | 7250 psi | 2 in/min; ASTM Test | |||
| Elongation at Break | >= 50 % | >= 50 % | 50mm/min, Nominal strain; ISO 527 | ||
| >= 100 % | >= 100 % | 2 in/min; ASTM Test | |||
| Elongation at Yield | 4.5 % | 4.5 % | 50mm/min; ISO 527 | ||
| 5.0 % | 5.0 % | 2 in/min; ASTM Test | |||
| Tensile Modulus | 1.70 GPa | 247 ksi | 1mm/min; ISO 527 | ||
| Flexural Strength | 50.0 MPa | 7250 psi | ISO Data | ||
| 69.0 MPa | 10000 psi | ASTM Test | |||
| 9.50 MPa @Temperature 120 °C | 1380 psi @Temperature 248 °F | ASTM Test | |||
| 10.0 MPa @Temperature 93.0 °C | 1450 psi @Temperature 199 °F | ASTM Test | |||
| 15.0 MPa @Temperature 65.0 °C | 2180 psi @Temperature 149 °F | ASTM Test | |||
| 105 MPa @Temperature -40.0 °C | 15200 psi @Temperature -40.0 °F | ASTM Test | |||
| Flexural Modulus | 1.45 GPa | 210 ksi | ISO Data | ||
| 1.73 GPa | 251 ksi | ASTM Test | |||
| 0.190 GPa @Temperature 120 °C | 27.6 ksi @Temperature 248 °F | ASTM Test | |||
| 0.220 GPa @Temperature 93.0 °C | 31.9 ksi @Temperature 199 °F | ASTM Test | |||
| 0.375 GPa @Temperature 65.0 °C | 54.4 ksi @Temperature 149 °F | ASTM Test | |||
| Izod Impact, Notched | 5.90 J/cm @Thickness 3.17 mm | 11.1 ft-lb/in @Thickness 0.125 in | ASTM Test | ||
| Charpy Impact Unnotched | NB | NB | ISO 179 | ||
| Charpy Impact, Notched | 4.00 J/cm2 | 19.0 ft-lb/in2 | ISO 179 | ||
| 0.900 J/cm2 @Temperature -30.0 °C | 4.28 ft-lb/in2 @Temperature -22.0 °F | ISO 179 | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| 220 °C | 428 °F | ASTM Test | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | ISO 75 | ||
| 55.0 °C | 131 °F | ASTM Test | |||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Commercial Status | Active America | ||||
| Form | Pellets | ||||
| Impact Modified | Yes | ||||
| Primary Processing Technique | Extrusion | ||||
| Processing | Profile Extrusion | ||||
| Sheet extrusion | |||||
| Special characteristic | Heat stabilized or stable to heat | ||||
| UL.UL-C | Yes | ||||