- 熔體流動速率 [g/10min]: 33.3
- 密度 [g/cm3]: 1.33
- 吸水率 [%]: 5.9
- 缺口沖擊強度: 32.0
- 拉伸強度 [MPa]: 100.0
- 彎曲模量 [MPa]: 4.70
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.33 g/cc | 0.0480 lb/in3 | ISO 1183 | ||
| Water Absorption | 5.9 - 6.5 % | 5.9 - 6.5 % | ISO 62 | ||
| Moisture Absorption at Equilibrium | 1.8 - 2.2 % | 1.8 - 2.2 % | (23°C/50% R.H.); ISO 62 | ||
| Viscosity Test | 160 cm3/g | 160 cm3/g | Viscosity number; ISO 307 | ||
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | |||
| Melt Flow | 33.3 g/10 min @Load 5.00 kg, Temperature 275 °C | 33.3 g/10 min @Load 11.0 lb, Temperature 527 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 100 MPa | 14500 psi | 50mm/min; ISO 527 | ||
| Elongation at Yield | 10 % | 10 % | 50mm/min; ISO 527 | ||
| Modulus of Elasticity | 5.30 GPa | 769 ksi | ISO 527 | ||
| Flexural Strength | 89.6 MPa | 13000 psi | ISO 178 | ||
| Flexural Modulus | 4.70 GPa | 682 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 32.0 kJ/m2 | 15.2 ft-lb/in2 | ISO 180/A | ||
| Charpy Impact Unnotched | 11.0 J/cm2 | 52.4 ft-lb/in2 | ISO 179/1eU | ||
| Charpy Impact, Notched | 3.50 J/cm2 | 16.7 ft-lb/in2 | ISO 179/1eA | ||
| Tensile Creep Modulus, 1000 hours | 3000 MPa | 435000 psi | ISO 899 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+10 ohm-cm | 1.00e+10 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+10 ohm | 1.00e+10 ohm | IEC 60093 | ||
| Dielectric Constant | 6.8 @Frequency 1.00e+6 Hz | 6.8 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Dissipation Factor | 0.20 @Frequency 1.00e+6 Hz | 0.20 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Comparative Tracking Index | 550 V | 550 V | Test Solution A; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| Thermal Conductivity | 0.350 W/m-K | 2.43 BTU-in/hr-ft2-°F | DIN 52612 | ||
| Melting Point | 220 °C | 428 °F | DIN 53765 | ||
| Maximum Service Temperature, Air | 180 °C | 356 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | Injection-molding/Extrusion | ||
| Mold Temperature | 80.0 - 90.0 °C | 176 - 194 °F | Injection-molding | ||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Commercial Status | North America and Europe | ||||
| Form | Pellets | ||||
| Impact Modified | Yes | ||||
| Primary Processing Technique | Injection Molding | ||||
| Processing | Injection Molding | ||||
| Special characteristic | Heat stabilized or stable to heat | ||||