- 熔體流動速率 [g/10min]: 8.0
- 密度 [g/cm3]: 1.13
- 吸水率 [%]: 9.5
- 拉伸強度 [MPa]: 45.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in3 | dry; ISO 1183 | ||
| Water Absorption | 9.5 % | 9.5 % | beginning dry; ISO 62 | ||
| Moisture Absorption at Equilibrium | 2.6 % | 2.6 % | beginning dry (23°C/50% R.H.); ISO 62 | ||
| Relative Viscosity | 5.0 cP | 5.0 cP | ISO Test; 96 % SAV | ||
| Viscosity Test | 320 cm3/g | 320 cm3/g | Viscosity number | ||
| Linear Mold Shrinkage | 0.0090 cm/cm | 0.0090 in/in | ASTM Data; MD | ||
| Melt Flow | 8.0 g/10 min @Load 5.00 kg, Temperature 275 °C | 8.0 g/10 min @Load 11.0 lb, Temperature 527 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 45.0 MPa | 6530 psi | 50mm/min; ISO 527 | ||
| Elongation at Break | >= 50 % | >= 50 % | 50mm/min, Nominal strain; ISO 527 | ||
| Elongation at Yield | 20 % | 20 % | 50mm/min; ISO 527 | ||
| Tensile Modulus | 1.00 GPa | 145 ksi | 1mm/min; ISO 527 | ||
| Tensile Creep Modulus, 1 hour | 950 MPa | 138000 psi | ISO 899 | ||
| Tensile Creep Modulus, 1000 hours | 850 MPa | 123000 psi | ISO 899 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| 220 °C | 428 °F | ASTM Test | |||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Commercial Status | North America and Europe | ||||
| FDA | 21 CFR 177.1500 | ||||
| Form | Pellets | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Film Extrusion | ||||
| Processing | Film Extrusion | ||||
| Profile Extrusion | |||||