- 密度 [g/cm3]: 1.36
- 吸水率 [%]: 6.2
- 缺口沖擊強度: 0.45
- 彎曲強度 [MPa]: 85.0
- 彎曲模量 [MPa]: 4.00
- 熱變形溫度 [℃]: 195.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in3 | ISO 1183 | ||
| Water Absorption | 6.2 % | 6.2 % | ISO 62 | ||
| Moisture Absorption at Equilibrium | 2.4 % | 2.4 % | 23°C/50% R.H.; ISO 62 | ||
| Viscosity Test | 150 cm3/g | 150 cm3/g | Viscosity number | ||
| Linear Mold Shrinkage | 0.0090 cm/cm | 0.0090 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 76.0 MPa | 11000 psi | 0.2 in/min; ASTM Test | ||
| Tensile Strength, Ultimate | 85.0 MPa | 12300 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 5.0 % | 5.0 % | 0.2 in/min; ASTM Test | ||
| 15 % | 15 % | 5mm/min; ISO 527 | |||
| Tensile Modulus | 4.60 GPa | 667 ksi | 1mm/min; ISO 527 | ||
| 5.17 GPa | 750 ksi | ASTM Test | |||
| Flexural Modulus | 4.00 GPa | 580 ksi | ISO Data | ||
| 4.10 GPa | 595 ksi | ASTM Test | |||
| Izod Impact, Notched | 0.450 J/cm @Temperature -40.0 °C | 0.843 ft-lb/in @Temperature -40.0 °F | ASTM Test | ||
| 0.640 J/cm @Thickness 3.17 mm | 1.20 ft-lb/in @Thickness 0.125 in | ASTM Test | |||
| Izod Impact, Notched (ISO) | 6.50 kJ/m2 | 3.09 ft-lb/in2 | ISO Test | ||
| Charpy Impact Unnotched | 22.0 J/cm2 | 105 ft-lb/in2 | ISO 179 | ||
| 14.5 J/cm2 @Temperature -30.0 °C | 69.0 ft-lb/in2 @Temperature -22.0 °F | ISO 179 | |||
| Charpy Impact, Notched | 0.800 J/cm2 | 3.81 ft-lb/in2 | ISO 179 | ||
| 0.700 J/cm2 @Temperature -30.0 °C | 3.33 ft-lb/in2 @Temperature -22.0 °F | ISO 179 | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 | ||
| Dielectric Constant | 3.5 @Frequency 1.00e+6 Hz | 3.5 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Dissipation Factor | 0.020 @Frequency 1.00e+6 Hz | 0.020 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| 0.020 @Frequency 100 Hz | 0.020 @Frequency 100 Hz | IEC 60250 | |||
| Comparative Tracking Index | 450 V | 450 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 30.0 μm/m-°C @Temperature -30.0 - 30.0 °C | 16.7 μin/in-°F @Temperature -22.0 - 86.0 °F | ASTM Test | ||
| CTE, linear, Parallel to Flow | 65.0 μm/m-°C | 36.1 μin/in-°F | ISO 11359 | ||
| CTE, linear, Transverse to Flow | 60.0 μm/m-°C | 33.3 μin/in-°F | ISO 11359 | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| 220 °C | 428 °F | ASTM Test | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 195 °C | 383 °F | ASTM Test | ||
| 195 °C | 383 °F | ISO 75 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 120 °C | 248 °F | ASTM Test | ||
| 120 °C | 248 °F | ISO 75 | |||
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |||
| HB @Thickness 3.20 mm | HB @Thickness 0.126 in | ||||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Commercial Status | Active America | ||||
| Form | Pellets | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||
| Processing | Injection Molding | ||||
| Special characteristic | Heat stabilized or stable to heat | ||||