- 密度 [g/cm3]: 1.32
- 缺口沖擊強度: 1.98
- 拉伸強度 [MPa]: 130.0
- 彎曲模量 [MPa]: 8.00
- 熱變形溫度 [℃]: 200.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.32 g/cc | 0.0477 lb/in3 | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 130 MPa | 18900 psi | ASTM D638 |
| Elongation at Break | 4.5 % | 4.5 % | ASTM D638 |
| Flexural Modulus | 8.00 GPa @Thickness 3.17 mm | 1160 ksi @Thickness 0.125 in | ASTM D790 |
| Izod Impact, Notched | 1.98 J/cm @Thickness 3.17 mm | 3.71 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Izod Impact, Unnotched | 5.34 J/cm @Thickness 3.17 mm | 10.0 ft-lb/in @Thickness 0.125 in | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | >= 200 °C | >= 392 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 195 °C | 383 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.57 mm | HB @Thickness 0.0620 in | |